A Comparative Thermoacoustic Insulation Study of Silica Aerogels Reinforced with Reclaimed Textile Fibres: Cotton, Polyester and Wool.

Silica aerogels are highly porous materials with exceptional thermal insulation performance. They become even more attractive if combined thermal and acoustic insulation is achieved. Silica aerogel composites reinforced with fibres are an ingenious way to surpass the fragility stemmed from the aerogel's intrinsic porosity, and textile fibres are good sound absorption materials.

Cellulosic films obtained from the treatment of sugarcane bagasse fibers with N-methylmorpholine-N-oxide (NMMO).

Ethanol/water organosolv pulping was used to obtain sugarcane bagasse pulp that was bleached with sodium chlorite. This bleached pulp was used to obtain cellulosic films that were further evaluated by Fourier transform infrared (FTIR) spectroscopy, thermogravimetric analysis (TGA), and scanning electron microscopy (SEM). A good film formation was observed when temperature of 74 degrees C and baths of distilled water were used, which after FTIR, TGA, and SEM analysis indicated no significant difference between the reaction times.

Carboxymethylcellulose obtained by ethanol/water organosolv process under acid conditions.

Sugar cane bagasse pulps were obtained by ethanol/water organosolv process under acid and alkaline conditions. The best condition of acid pulping for the sugarcane bagasse was 0.02 mol/L sulfuric acid at 160 degrees C, for 1 h, whereas the best condition for alkaline pulping was 5% sodium hydroxide (base pulp) at 160 degrees C, for 3 h.