Changes in the mechanical properties of chemically treated bovine pericardium after a short uniaxial cyclic test.

The mechanical behavior of calf pericardium, a biomaterial utilized in the manufacture of cardiac bioprostheses, in response to a short tensile cyclic test has been evaluated. The trial involved 120 samples cut longitudinally or transversely, subjected to 10 cycles until a stress of between 1 and 3 MPa was reached. Tests of hardness and tear propagation were performed, and the results were compared with a control series.

Fatigue behaviour of young ostrich pericardium.

Young ostrich pericardia (biomaterial under study for manufacturing cardiac valve leaflets), has been subjected to biaxial tension fatigue until breakage. Supraphysiological values of pressure (1 to 6 atm) have been employed to accelerate damage and, therefore, to reduce testing time but at physiological frequency in order to avoid viscoelastic behaviour changes. The lifetime fatigue curves have been obtained and large scatter has been observed in the results but this can be strongly reduced with adequate material selection.