Height dependent molecular trapping in stacked cyclic porphyrin nanorings.

Stacked layers of cyclic porphyrin nanorings constitute nanoscale receptacles with variable height and diameter which preferentially adsorb sublimed molecules. Using scanning tunnelling microscopy we determine the filling capacity of these nanoring traps, and the dependence of adsorbate capture on stack height and diameter.

Fullerenes as adhesive layers for mechanical peeling of metallic, molecular and polymer thin films.

We show that thin films of C60 with a thickness ranging from 10 to 100 nm can promote adhesion between a Au thin film deposited on mica and a solution-deposited layer of the elastomer polymethyldisolaxane (PDMS). This molecular adhesion facilitates the removal of the gold film from the mica support by peeling and provides a new approach to template stripping which avoids the use of conventional adhesive layers. The fullerene adhesion layers may also be used to remove organic monolayers and thin films as well as two-dimensional polymers which are pre-formed on the gold surface and have monolayer thickness.

Mechanical stiffening of porphyrin nanorings through supramolecular columnar stacking.

Solvent-induced aggregates of nanoring cyclic polymers may be transferred by electrospray deposition to a surface where they adsorb as three-dimensional columnar stacks. The observed stack height varies from single rings to four stacked rings with a layer spacing of 0.32 ± 0.