Nanoscale Metastable ε-FeN Ferromagnetic Materials by Self-Sustained Reactions.

A single-step method for the preparation of metastable ε-FeN nanoparticles by combustion of reactive gels containing iron nitrate (Fe(NO)) and hexamethylenetetramine (CHN) in an inert atmosphere is reported. The results of Fourier transform infrared spectroscopy (FTIR) and thermal analysis coupled with dynamic mass spectrometry revealed that the exothermic decomposition of a coordination complex formed between Fe(NO) and HMTA is responsible for the formation of ε-FeN nanoscale particles with sizes of 5-15 nm. The magnetic properties between 5 and 350 K are characterized using a superconducting quantum interference device (SQUID) magnetometer, revealing a ferromagnetic behavior with a low-temperature magnetic moment of 1.

Field-free manipulation of magnetization alignments in a Fe/GaAs/GaMnAs multilayer by spin-orbit-induced magnetic fields.

We investigate the process of selectively manipulating the magnetization alignment in magnetic layers in the Fe/GaAs/GaMnAs structure by current-induced spin-orbit (SO) magnetic field. The presence of such fields manifests itself through the hysteretic behavior of planar Hall resistance observed for two opposite currents as the magnetization in the structure switches directions. In the case of the Fe/GaAs/GaMnAs multilayer, hystereses are clearly observed when the magnetization switches direction in the GaMnAs layer, but are negligible when magnetization transitions occur in Fe.

Selective Chemical Response of Transition Metal Dichalcogenides and Metal Dichalcogenides in Ambient Conditions.

To fabricate practical devices based on semiconducting two-dimensional (2D) materials, the source, channel, and drain materials are exposed to ambient air. However, the response of layered 2D materials to air has not been fully elucidated at the molecular level. In the present report, the effects of air exposure on transition metal dichalcogenides (TMD) and metal dichalcogenides (MD) are studied using ultrahigh-vacuum scanning tunneling microscopy (STM).

Measurement of coherence decay in GaMnAs using femtosecond four-wave mixing.

The application of femtosecond four-wave mixing to the study of fundamental properties of diluted magnetic semiconductors ((s,p)-d hybridization, spin-flip scattering) is described, using experiments on GaMnAs as a prototype III-Mn-V system.  Spectrally-resolved and time-resolved experimental configurations are described, including the use of zero-background autocorrelation techniques for pulse optimization.  The etching process used to prepare GaMnAs samples for four-wave mixing experiments is also highlighted.

Giant Zeeman splitting in nucleation-controlled doped CdSe:Mn2+ quantum nanoribbons.

Doping of semiconductor nanocrystals by transition-metal ions has attracted tremendous attention owing to their nanoscale spintronic applications. Such doping is, however, difficult to achieve in low-dimensional strongly quantum confined nanostructures by conventional growth procedures. Here we demonstrate that the incorporation of manganese ions up to 10% into CdSe quantum nanoribbons can be readily achieved by a nucleation-controlled doping process.

Spin-polarizable excitonic luminescence in colloidal Mn2+-doped CdSe quantum dots.

The photoluminescence of colloidal Mn2+-doped CdSe nanocrystals has been studied as a function of nanocrystal diameter. These nanocrystals are shown to be unique among colloidal doped semiconductor nanocrystals reported to date in that quantum confinement allows tuning of the CdSe bandgap energy across the Mn2+ excited-state energies. At small diameters, the nanocrystal photoluminescence is dominated by Mn 2+ emission.