Alumina-Toughened-Zirconia with Low Wear Rate in Ball-on-Flat Tribological Tests at Temperatures to 500 °C.

An alumina-toughened zirconia (ATZ) material, fabricated using a procedure consisting of the common sintering of two different zirconia powders, was tested using the ball-on-disc method in a temperature range between room temperature and 500 °C. Corundum balls were used as a counterpart. The ATZ composite behaviour during tests was compared with that of commonly used α-alumina and tetragonal zirconia sintered samples.

Hydrothermal Aging of ATZ Composites Based on Zirconia Made of Powders with Different Yttria Content.

The presented work concerns the development and investigation of three different grades of ZrO materials containing AlO particles (ATZ-Alumina Toughened Zirconia ceramics with 2.3-20 vol.% of alumina).