Self-tapping ability of carbon fibre reinforced polyetheretherketone suture anchors.

An experimental and computational investigation of the self-tapping ability of carbon fibre reinforced polyetheretherketone (CFR-PEEK) has been conducted. Six CFR-PEEK suture anchor designs were investigated using PEEK-OPTIMA® Reinforced, a medical grade of CFR-PEEK. Experimental tests were conducted to investigate the maximum axial force and torque required for self-taping insertion of each anchor design.

Mechanical and in vitro investigation of a porous PEEK foam for medical device implants.

Purpose: Implantable-grade polyetheretherketone (PEEK-OPTIMA®) is a high-performance thermoplastic that has been used in implant devices such as spinal-fusion cages since its introduction in 1999. Here, a new porous PEEK version was investigated.

Methods: Porous PEEK was fabricated using industrial scale relevant methods of compounding with porogen filler, extrusion, and subsequent extraction with water at supercritical temperatures and pressures.

Biotribological study of large diameter ceramic-on-CFR-PEEK hip joint including fluid uptake, wear and frictional heating.

A novel material combination of a large diameter Biolox(®) Delta zirconia-toughened-alumina (ZTA) head and a pitch-based carbon fibre reinforced poly ether-ether-ketone (CFR-PEEK) MOTIS(®) cup has been studied. The acetabular cups were inclined at three angles and tested using Durham Hip Simulators. The different inclination angles used did not have a significant effect on the wear rates (ANOVA, p = 0.

Macrophage reactivity to different polymers demonstrates particle size- and material-specific reactivity: PEEK-OPTIMA(®) particles versus UHMWPE particles in the submicron, micron, and 10 micron size ranges.

Biologic reactivity to orthopedic implant debris is generally the main determinant of long-term clinical performance where released polymeric particles of Ultra-high molecular weight polyethylene (UHMWPE) remain the most prevalent debris generated from metal-on-polymer bearing total joint arthroplasties. Polymeric alternatives to UHMWPE such as polyetherether-ketone (PEEK) may have increased wear resistance but the bioreactivity of PEEK-OPTIMA particles on peri-implant inflammation remains largely uncharacterized. We evaluated human monocyte/macrophage responses (THP-1s and primary human) when challenged by PEEK-OPTIMA, UHMWPE, and X-UHMWPE particles of three particle sizes (0.

The in vitro response of human osteoblasts to polyetheretherketone (PEEK) substrates compared to commercially pure titanium.

Polyetheretherketone (PEEK) is used as an alternative to titanium in medical devices. Previous in vitro studies examining PEEK have differed in their choice of polymer variant [PEEK or carbon-fiber reinforced PEEK (CFR-PEEK)], source of polymer (some of which are no longer available or for implantation) and cell type. While all studies demonstrated favorable cytocompatibility of the PEEK material, no studies are available which reflect the current state of the art of the material.

Implantable PEEK extends the options.

The availability of a performance polymer alongside the established metals and ceramics for orthopaedic applications offers more choice and capabilities.

Porcine collagen crosslinking, degradation and its capability for fibroblast adhesion and proliferation.

Porcine dermal collagen permanently crosslinked with hexamethylene diisocyanate was investigated for its suitability as a dermal tissue engineering matrix. It was found that the chemically crosslinked collagen had far fewer free lysine groups per collagen molecule than did the uncrosslinked matrix. The ability of the matrix to support human primary fibroblast outgrowth from explants was compared for matrices that had been presoaked in various solutions, including fibroblast media, cysteine and phosphate buffered saline (PBS).