Tissue response to experimental dental cements prepared from a modified powder glass composition.

The present work seeks to evaluate the biocompatibility of experimental glass ionomer cements (GIC) prepared from niobium-calcium fluoro-alumino-silicate glass powder and two commercial GICs. The GICs were implanted into the subcutaneous connective tissue of sixty rats. The rats were sacrificed during four varying time periods: 7, 15, 30, and 60 days and histopathological examinations were then performed.

Determination of the properties of an experimental glass polyalkenoate cement prepared from niobium silicate powder containing fluoride.

Objectives: The purpose of this paper is to modify the conventional calcium fluoro-alumino-silicate glass, which is used in the formation of glass ionomer cements (CIGs) by the niobium addition and to study the properties of GICs obtained.

Materials And Methods: Sol-gel process was used to prepare the powder at lower temperature than fusion method. Glass-ceramic powder obtained in this way was used to prepare the GICs.

In vitro biocompatibility of a novel membrane of the composite poly(vinylidene-trifluoroethylene)/barium titanate.

This study was aimed at investigating the in vitro biocompatibility of a novel membrane of the composite poly(vinylidene-trifluoroethylene)/barium titanate (P(VDF-TrFE)/BT). Osteoblastic cells were obtained from human alveolar bone fragments and cultured under standard osteogenic condition until subconfluence. First passaged cells were cultured on P(VDF-TrFE)/BT and expanded polytetrafluoroethylene (e-PTFE--control) membranes in 24-well plates.