Swift heavy ion-beam induced amorphization and recrystallization of yttrium iron garnet.

Pure and (Ca and Si)-substituted yttrium iron garnet (Y3Fe5O12 or YIG) epitaxial layers and amorphous films on gadolinium gallium garnet (Gd3Ga5O12, or GGG) single crystal substrates were irradiated by 50 MeV (32)Si and 50 MeV (or 60 MeV) (63)Cu ions for electronic stopping powers larger than the threshold value (~4 MeV μm(-1)) for amorphous track formation in YIG crystals. Conductivity data of crystalline samples in a broad ion fluence range (10(11)-10(16) cm(-2)) are modeled with a set of rate equations corresponding to the amorphization and recrystallization induced in ion tracks by electronic excitations. The data for amorphous layers confirm that a recrystallization process takes place above ~10(14) cm(-2).

Tracing temperature in a nanometer size region in a picosecond time period.

Irradiation of materials with either swift heavy ions or slow highly charged ions leads to ultrafast heating on a timescale of several picosecond in a region of several nanometer. This ultrafast local heating result in formation of nanostructures, which provide a number of potential applications in nanotechnologies. These nanostructures are believed to be formed when the local temperature rises beyond the melting or boiling point of the material.

Amorphization of nanocrystalline monoclinic ZrO2 by swift heavy ion irradiation.

Bulk ZrO(2) polymorphs generally have an extremely high amorphization tolerance upon low energy ion and swift heavy ion irradiation in which ballistic interaction and ionization radiation dominate the ion-solid interaction, respectively. However, under very high-energy irradiation by 1.33 GeV U-238, nanocrystalline (40-50 nm) monoclinic ZrO(2) can be amorphized.

Thick optical waveguides in lithium niobate induced by swift heavy ions (approximately 10 MeV/amu) at ultralow fluences.

Heavy mass ions, Kr and Xe, having energies in the approximately 10 MeV/amu range have been used to produce thick planar optical waveguides at the surface of lithium niobate (LiNbO3). The waveguides have a thickness of 40-50 micrometers, depending on ion energy and fluence, smooth profiles and refractive index jumps up to 0.04 (lambda = 633 nm).

Temperature and pressure spikes in ion-beam cancer therapy.

The inelastic thermal spike model is applied to liquid water in relation to high-energy 12C6+ beams (hundreds of MeV/u) used for cancer therapy. The goal of this project is to calculate the heat transfer in the vicinity of the incident-ion track. Thermal spike calculations indicate a very large temperature increase in the vicinity of ion tracks near the Bragg peak during the time interval from 10(-15) to 10(-9) s after the ion's passage and an increase in pressure, as large as tens of MPa, can be induced during that time.