Exploring the Interplay between Tribocorrosion and Surface Chemistry of the ASTM F139 Surgical Stainless Steel in Phosphate-Buffered Saline Solution.

Surgical ASTM F139 stainless steel is used for temporary fixtures in the biomedical field. Tribocorrosion is a major concern in this application. The aim of the present work was to study the interplay between tribocorrosion behavior and the surface chemistry of the ASTM F139 stainless steel in phosphate-buffered saline solution (PBS).

Corrosion fatigue of biomedical metallic alloys: mechanisms and mitigation.

Cyclic stresses are often related to the premature mechanical failure of metallic biomaterials. The complex interaction between fatigue and corrosion in the physiological environment has been subject of many investigations. In this context, microstructure, heat treatments, plastic deformation, surface finishing and coatings have decisive influence on the mechanisms of fatigue crack nucleation and growth.

Corrosion processes of physical vapor deposition-coated metallic implants.

Protecting metallic implants from the harsh environment of physiological fluids is essential to guaranteeing successful long-term use in a patient's body. Chemical degradation may lead to the failure of an implant device in two different ways. First, metal ions may cause inflammatory reactions in the tissues surrounding the implant and, in extreme cases, these reactions may inflict acute pain on the patient and lead to loosening of the device.