Water-based route to colloidal Mn-doped ZnSe and core/shell ZnSe/ZnS quantum dots.

Relatively monodisperse and highly luminescent Mn(2+)-doped zinc blende ZnSe nanocrystals were synthesized in aqueous solution at 100 °C using the nucleation-doping strategy. The effects of the experimental conditions and of the ligand on the synthesis of nanocrystals were investigated systematically. It was found that there were significant effects of molar ratio of precursors and heating time on the optical properties of ZnSe:Mn nanocrystals.

Folic acid-conjugated core/shell ZnS:Mn/ZnS quantum dots as targeted probes for two photon fluorescence imaging of cancer cells.

This work presents a novel approach to producing water soluble manganese-doped core/shell ZnS/ZnS quantum dots (ZnS:Mn/ZnS). The Mn-doped ZnS core was prepared through a nucleation doping strategy and a ZnS shell was grown on ZnS:Mn d-dots by decomposition of Zn(2+)-3-mercaptopropionic acid (MPA) complexes at 100 °C. It was found that the Mn2+(4)T1→6A1 fluorescence emission at ∼590 nm significantly increased after growth of the shell when the Mn2+ doping content was 4.