Tuning High and Low Temperature Foaming Behavior of Linear and Long-Chain Branched Polypropylene via Partial and Complete Melting.

While existing foam studies have identified processing parameters, such as high-pressure drop rate, and engineering measures, such as high melt strength, as key factors for improving foamability, there is a conspicuous absence of studies that directly relate foamability to material properties obtained from fundamental characterization. To bridge this gap, this work presents batch foaming studies on one linear and two long-chain branched polypropylene (PP) resins to investigate how foamability is affected by partial melting (Method 1) and complete melting followed by undercooling (Method 2). At temperatures above the melting point, similar expansion was obtained using both foaming procedures within each resin, while the PP with the highest strain hardening ratio (13) exhibited the highest expansion ratio (45 ± 3).

Tunable Tensile Properties of Polypropylene and Polyethylene Terephthalate Fibrillar Blends through Micro-/Nanolayered Extrusion Technology.

Fiber-reinforcement is a well-established technique to enhance the tensile properties of polymer composites, which is achieved via changing the reinforcing material concentration and orientation. However, the conventional method can be costly and may lead to poor compatibility issues. To overcome these challenges, we demonstrate the use of micro-/nanolayer (MNL) extrusion technology to tune the mechanical properties of polypropylene (PP)/polyethylene terephthalate (PET) fibrillar blends.