Alignment control of self-assembled organosiloxane films derived from alkyloligosiloxane amphiphiles.

Transparent and continuous organosiloxane films with macroscopically oriented mesostructures were prepared by dip-coating a substrate, on which a rubbing-treated polyimide film is formed, with hydrolyzed solutions of oligosiloxane precursors (C(n)H(2n+1)Si(OSi(OMe)(3))(3)). The structure of the films depends on the alkyl chain length of the precursors such that films with two-dimensional (2D) hexagonal and lamellar structures are obtained when n = 10 and 16, respectively. In the 2D hexagonal film, the cylindrical organic moieties are aligned perpendicular to the rubbing direction in the plane of the film over the whole film thickness.