Fabrication of Graphene-Polyimide Nanocomposites with Superior Electrical Conductivity.

We report on the fabrication of a novel class of lightweight materials, polyimide-graphene nanocomposites (0.01-5 vol %), with tunable electrical conductivity. The graphene-polyimide nanocomposites exhibit an ultra-low graphene percolation threshold of 0.

Self-Healing of Core-Shell Magnetic Polystyrene Nanocomposites.

High heat generation is reported in core-shell magnetic nanoparticle polystyrene (PS) nanocomposites (3.5, 10 wt %) when they are placed in a high-frequency ac magnetic field. These magnetic nanoparticles with cobalt iron oxide core and manganese iron oxide shell were synthesized and characterized by wide-angle X-ray scattering (WAX), thermal gravimetric analysis (TGA), transmission electron microscopy (TEM), and ac field gradient magnetometery.

Carbon nanotube epoxy nanocomposites: the effects of interfacial modifications on the dynamic mechanical properties of the nanocomposites.

Surface functionalization of pretreated carbon nanotubes (CNT) using aromatic, aliphatic, and aliphatic ether diamines was performed. The pretreatment of the CNT consisted of either acid- or photo-oxidation. The acid treated CNT had a higher initial oxygen content compared to the photo-oxidized CNT and this resulted in a higher density of functionalization.

Graphene polyimide nanocomposites; thermal, mechanical, and high-temperature shape memory effects.

Flexible graphene polyimide nanocomposites (0.1-4 wt %) with superior mechanical properties over those of neat polyimide resin have been prepared by solution blending. Imide moieties were grafted to amine-functionalized graphene using a step-by-step condensation and thermal imidization method.

Transparent large-strain thermoplastic polyurethane magnetoactive nanocomposites.

Organically modified superparamagnetic MnFe(2)O(4)/thermoplastic polyurethane elastomer (TPU) nanocomposites (0.1-8 wt %) were prepared by solvent mixing followed by solution casting. Linear aliphatic alkyl chain modification of spherical MnFe(2)O(4) provided compatibility with the TPU containing a butanediol extended polyester polyol-MDI.