Structural characteristics of activated carbons and ibuprofen adsorption affected by bovine serum albumin.

Structural characteristics of a series of MAST carbons were studied using scanning electron microscopy images and the nitrogen adsorption isotherms analyzed with several models of pores and different adsorption equations. A developed model of pores as a mixture of gaps between spherical nanoparticles and slitlike pores was found appropriate for MAST carbons. Adsorption of ibuprofen [2-(4-isobutylphenyl)propionic acid] on activated carbons possessing different pore size distributions in protein-free and bovine serum albumin (BSA)-containing aqueous solutions reveals the importance of the contribution of mesopores to the total porosity of adsorbents.

Preparation of novel mesoporous carbons for the adsorption of an inflammatory cytokine (IL-1 beta).

Mesoporous carbons derived from two types of sulphonated styrene divinylbenzene copolymers (Macronet MN500HS and CT275, Purolite International Ltd) were produced and their adsorptive capacity for the proinflammatory cytokine IL-1 beta (MW 14.4 kDa) determined. The carbons produced had surface areas from 400 to 1200 m(2)g(-1) and pore volume between 0.

Characterisation of novel modified active carbons and marine algal biomass for the selective adsorption of lead.

This paper discusses the sorption performance of novel materials for the removal of lead(II) and copper(II) from near-neutral aqueous solutions. Active carbons with surface heteroatoms of oxygen and phosphorus have been prepared. The surface functional groups display weakly acidic ion exchange characteristics.

Adsorption of cadmium by activated carbon cloth: influence of surface oxidation and solution pH.

The surface of activated carbon cloth (ACC), based on polyacrylonitrile fibre as a precursor, was oxidised using nitric acid, ozone and electrochemical oxidation to enhance cadmium ion exchange capacity. Modified adsorbents were physically and chemically characterised by pH titration, direct titration, X-ray photoelectron spectroscopy, elemental analysis, surface area and porosimetry, and scanning electron microscopy. BET surface area decreased after oxidation, however, the total ion exchange capacity increased by a factor of approximately 3.