Quick Preparation of Moisture-Saturated Carbon Fiber-Reinforced Plastics and Their Accelerated Ageing Tests Using Heat and Moisture.

A quick method involving the control of heat and water vapor pressure for preparing moisture-saturated carbon fiber-reinforced plastics (CFRP, 8 unidirectional prepreg layers, 1.5 mm thickness, epoxy resin) has been developed. The moisture-saturated CFRP sample was obtained at 120 °C and 0.

Biobased carbon content of resin extracted from polyethylene composite by carbon-14 concentration measurements using accelerator mass spectrometry.

An estimation procedure for biobased carbon content of polyethylene composite was studied using carbon-14 ((14)C) concentration ratios as measured by accelerated mass spectrometry (AMS). Prior to the measurement, additives and fillers in composites should be removed because they often contain a large amount of biobased carbon and may shift the estimation. Samples of resin with purity suitable for measurement were isolated from composites with a Soxhlet extractor using heated cyclohexanone.

Chemical synthesis of fully biomass-based poly(butylene succinate) from inedible-biomass-based furfural and evaluation of its biomass carbon ratio.

We have produced fully biomass-based poly(butylene succinate) (PBS) from furfural produced from inedible agricultural cellulosic waste. Furfural was oxidized to give fumaric acid. Fumaric acid was hydrogenated under high pressure with a palladium-rhenium/carbon catalyst to give 1,4-butanediol, and with a palladium/carbon catalyst to give succinic acid.

Possible incorporation of petroleum-based carbons in biochemicals produced by bioprocess--biomass carbon ratio measured by accelerator mass spectrometry.

The biomass carbon ratios of biochemicals related to biomass have been reviewed. Commercial products from biomass were explained. The biomass carbon ratios of biochemical compounds were measured by accelerator mass spectrometry (AMS) based on the (14)C concentration of carbons in the compounds.