In situ characterization of stresses, deformation and fracture of thin films using transmission X-ray nanodiffraction microscopy. Corrigendum.

Errors in variable subscripts, equations and Fig. 8 in Section 3.2 of the article by Lotze et al.

In situ characterization of stresses, deformation and fracture of thin films using transmission X-ray nanodiffraction microscopy.

The use of hard X-ray transmission nano- and microdiffraction to perform in situ stress and strain measurements during deformation has recently been demonstrated and used to investigate many thin film systems. Here a newly commissioned sample environment based on a commercially available nanoindenter is presented, which is available at the NanoMAX beamline at the MAX IV synchrotron. Using X-ray nanoprobes of around 60-70 nm at 14-16 keV and a scanning step size of 100 nm, we map the strains, stresses, plastic deformation and fracture during nanoindentation of industrial coatings with thicknesses in the range of several micrometres, relatively strong texture and large grains.

Imaging Ultrafast Dynamical Diffraction Wave Fronts in Strained Si with Coherent X Rays.

Dynamical diffraction effects in thin single crystals produce highly monochromatic parallel x-ray beams with a mutual separation of a few microns and a time delay of a few femtoseconds-the so-called echoes. This ultrafast diffraction effect is used at X-Ray Free Electron Lasers in self-seeding schemes to improve beam monochromaticity. Here, we present a coherent x-ray imaging measurement of echoes from Si crystals and demonstrate that a small surface strain can be used to tune their temporal delay.

Wire-Based Additive Manufacturing of Ti-6Al-4V Using Electron Beam Technique.

Electron beam freeform fabrication is a wire feed direct energy deposition additive manufacturing process, where the vacuum condition ensures excellent shielding against the atmosphere and enables processing of highly reactive materials. In this work, this technique is applied for the α + β-titanium alloy Ti-6Al-4V to determine suitable process parameter for robust building. The correlation between dimensions and the dilution of single beads based on selected process parameters, leads to an overlapping distance in the range of 70%-75% of the bead width, resulting in a multi-bead layer with a uniform height and with a linear build-up rate.

Fatigue Crack Growth of Electron Beam Melted Ti-6Al-4V in High-Pressure Hydrogen.

Titanium-based alloys are susceptible to hydrogen embrittlement (HE), a phenomenon that deteriorates fatigue properties. Ti-6Al-4V is the most widely used titanium alloy and the effect of hydrogen embrittlement on fatigue crack growth (FCG) was investigated by carrying out crack propagation tests in air and high-pressure H environment. The FCG test in hydrogen environment resulted in a drastic increase in crack growth rate at a certain Δ K, with crack propagation rates up to 13 times higher than those observed in air.