Aging resistant ZTA composite for dental applications: Microstructural, optical and mechanical characterization.

Objective: To synthesize a zirconia toughened alumina (ZTA) composite with 70% alumina reinforced by 30% zirconia for dental applications and to characterize its microstructure and optical properties for comparison with the isolated counterpart materials and a first-generation 3Y-TZP.

Methods: Disc-shaped specimens were divided in four groups (n = 70/material): (1) 3YSB-E (first generation 3Y-TZP), (2) Zpex (second generation 3Y-TZP), (3) alumina, and (4) ZTA-Zpex 70/30. After synthesis, ceramic powders were pressed, and green-body samples sintered following a predetermined protocol.

Refolding of endostatin from inclusion bodies using high hydrostatic pressure.

High hydrostatic pressure was used for concomitant solubilization and refolding of insoluble endostatin (ES) aggregated as inclusion bodies (IBs). High hydrostatic pressure (200 MPa or 2 kbar) was applied in combination with nondenaturing concentrations of guanidine hydrochloride. High levels of correctly folded ES (90 mg/L culture) were obtained after optimization/standardization of the procedure by applying pressures of 200 MPa for 16 h in 1.