Achieving property enhancements in dental resin composites via reduced concentrations of camphorquinone within a ternary initiator system.

Objectives: The study aimed to assess the impact of diphenyliodonium hexafluorophosphate (DPI) on the physicochemical properties of experimental resin composites (ECRs) featuring reduced concentrations of camphorquinone (CQ)/amine.

Methods: Five concentrations of CQ (0.125, 0.

Influence of different concentrations of an iodonium salt on properties of amine-free resins.

Objectives: to evaluate the effect of different concentrations of an iodonium salt on the degree of conversion, polymerisation rate, flexural strength and modulus of an amine-free photopolymerizable resin system.

Methods: Two series of UDMA/TEGDMA resin mixtures (1:1 mass ratio) containing 0, 0.5, 1.

Bis(4-methyl phenyl)iodonium as an alternative component to diphenyliodonium in camphorquinone-based ternary initiating systems.

Objective: To evaluate the influence of different co-initiators (diphenyliodonium hexafluorophosphate - DPI - and bis(4-methyl phenyl)iodonium hexafluorophosphate - BPI) on chemical and mechanical properties of resins.

Methods: Nine experimental resins (50% Bis-GMA and 50% TEGDMA, w/w) with 60 wt% filler particles were formulated. The initiating system used was camphorquinone (CQ-1 mol%) and ethyl dimethylaminobenzoate (EDAB-2 mol%).

Increased rates of photopolymerisation by ternary type II photoinitiator systems in dental resins.

To evaluate the effects of Type I and Type II photoinitiator systems on curing efficiency, degree of conversion (DC) and chemico-physical properties of resin based materials. A comonomer base containing 50%wt 2.2-bis[4-(2-hydroxy-3-methacryloxypropoxy)phenyl]propane (bis-GMA) and 50%wt triethyleneglycol dimethacrylate (TEGDMA) was formulated with either 0.

Influence of light-curing unit on the network structure and mechanical properties of model resin cements containing diphenyliodonium compared with a commercial reference.

Objective: To evaluate the effects of dyphenyliodonium hexafluorophosphate (DPI) on crosslink density (CLD), flexural strength (FS), and flexural modulus (FM) of a light-cured experimental resin cement compared with a commercial dual-cured cement.

Materials And Methods: Bis-GMA combined with TEGDMA (50-50%) was used as resin matrix. Silanated barium-aluminum-silica glass was used as inorganic filler.

Effect of diphenyliodonium hexafluorphosphate on resin cements containing different concentrations of ethyl 4-(dimethylamino)benzoate and 2-(dimethylamino)ethyl methacrylate as co-initiators.

Objective: The present study evaluated the influence of diphenyliodonium hexafluorphosphate (DPI) combined with two different amines [ethyl 4-(dimethylamino)benzoate (EDAB) and 2-(dimethylamino)ethyl methacrylate (DMAEMA)] on the properties of model resin cements.

Methods: A comonomer base containing a 1:1 mass ratio of 2.2-bis[4-(2-hydroxy-3-methacryloxypropoxy)phenyl]propane (bis-GMA) and triethyleneglycol dimethacrylate (TEGDMA) was obtained, after which 1mol% of camphorquinone and 0.

The effect of surface treatment and bonding procedures on the bond strength of silorane composite repairs.

Objective: The aim of this study was to evaluate the effect of surface treatments and adhesive protocols on the microtensile bond strength of a low-shrinkage composite repair.

Materials And Methods: Ninety-six blocks of composite resin Filtek LS were prepared using a half-hourglass-shaped silicone matrix. The specimens were storage for 24 h in distilled water and were randomly divided into the experimental (6) and negative control (2) groups (n = 12) according to the surface treatment (diamond bur and aluminum oxide sandblasting) and adhesive protocol (none; Filtek LS adhesive; phosphoric acid + Filtek LS adhesive; and phosphoric acid + silane + Filtek LS adhesive).

Mechanical properties and degree of conversion of etch-and-rinse and self-etch adhesive systems cured by a quartz tungsten halogen lamp and a light-emitting diode.

The aim of the present study was to evaluate the degree of conversion (DC), elastic modulus (E), and flexural strength (FS) of five adhesive systems (only the bonding component of both Scotchbond MP-SBMP and Clearfil Protect Bond-CP; Single Bond 2-SB2; One-up Bond F Plus-OUP; and P90 System Adhesive: primer-P90P and bond-P90B) cured with a quartz tungsten halogen (QTH) lamp and a light-emitting diode (LED). Two groups per adhesive were formed (n=5), according to the light source (quartz tungsten halogen-QTH: Demetron LC; and light-emitting diode-LED: UltraLume 5). Bar-shaped specimens were evaluated using three-point bending.

Photoelastic evaluation of the effect of composite formulation on polymerization shrinkage stress.

We compared polymerization stress in two commercial composites and three experimental composites made using camphorquinone (CQ) and/or phenylpropanedione (PPD) as photoinitiators. The internal surfaces of photoelastic resin discs with cylindrical cavities were roughened and treated with adhesive. Composites were divided into five groups: two commercial composites (Filtek Silorane and Filtek Z250) and three experimental composites with CQ/amine, CQ/PPD/amine, and PPD/amine.

Influence of sterilization method on the bond strength of caries-affected dentin.

This study evaluated the effect of sterilization method on the bond strength of caries-affected dentin before artificial caries development and after restoration. Twelve bovine incisors were sectioned perpendicularly to their long axes at 7 mm from the amelodentinal junction. They were painted with acid-resistant nail varnish, except on an exposed coronal dentin area.