Bonding Efficacy of Universal Adhesives to Fluorotic Enamel after Pre-conditioning with EDTA.

Purpose: To compare the effect of active pre-conditioning with 17% ethylenediaminetetraacetic acid (EDTA) vs 37% phosphoric acid (PA) on the resin-enamel microshear bond strength (µSBS), enamel-etching pattern, and in situ degree of conversion (in situ DC) of four universal adhesives on sound and fluorotic enamel.

Material And Methods: In this study, 448 extracted human molars (224 without fluorosis and 224 with fluorosis) were sectioned into four parts and divided into 16 experimental groups based on the enamel surface (sound or fluorotic enamel), adhesive (Clearfil Universal Bond [CUB], Futurabond U [FBU], iBond Universal [IBU], or Scotchbond Universal [SBU]), and enamel conditioning agent (PA or EDTA). The specimens were stored for 24 h and tested under shear stress at 1.

Influence of the mode of application of universal adhesive systems on adhesive properties to fluorotic enamel.

The objective of this study is to compare the resin-enamel bond strength (mμSBS), in-situ degree of conversion (DC), and the enamel-etching pattern (SEM/EDX) of universal adhesive systems when applied to sound and fluorotic enamel. Ninety-eight human molars were sectioned into 4 parts and divided into 24 groups according to 1) enamel surface (sound or fluorotic enamel), 2) adhesive system (Clearfil Universal Bond [CUB], Futurabond U [FBU], iBond Universal [IBU], and Scotchbond Universal [SBU]), and 3) application mode (etch-and-rinse [ER], active self-etch [Active-SE], and passive self-etch [Passive-SE]). Specimens were stored at 37 °C, for 24 hours and tested at 1.