Custom Synthesis of ZnO Nanowires for Efficient Ambient Air-Processed Solar Cells.

Nanostructuration of solar cells is an interesting approach to improve the photovoltaic conversion efficiency (PCE). This work aims at developing architectured 3D hybrid photovoltaic solar cells using ZnO nanowires (ZnONWs) as the electron transport layer (ETL) and nanocollectors of electrons within the active layer (AL). ZnONWs have been synthesized using a hydrothermal process with a meticulous control of the morphology.

Effects of non-homogeneity and oxide coating on silver nanowire networks under electrical stress: comparison between experiment and modeling.

Silver nanowire (AgNW) networks are among the most promising indium-free, flexible transparent electrodes for energy, lighting and heating devices. However, the lack of stability of such networks is a key factor that limits their industrial application. While applications require homogeneous networks, non-homogeneous AgNW networks are intentionally prepared in the present work to probe the mechanisms leading to failure under electrical stress.

Dynamic degradation of metallic nanowire networks under electrical stress: a comparison between experiments and simulations.

Metallic nanowire networks represent a promising solution for a new generation of transparent and flexible devices, including touch screens, solar cells and transparent heaters. They, however, lack stability under thermal and electrical stresses, often leading to the degradation of nanowires, which results in the loss of electrical percolation paths. We propose a comprehensive description of the degradation mechanism in a metallic nanowire network subjected to electrical stress.

New Antimony-Based Organic-Inorganic Hybrid Material as Electron Extraction Layer for Efficient and Stable Polymer Solar Cells.

Hybrid organic-inorganic materials are a new class of materials used as interfacial layers (ILs) in polymer solar cells (PSCs). A hybrid material, composed of antimony as the inorganic part and diaminopyridine as the organic part, is synthesized and described as a new material for application as the electron extraction layer (EEL) in PSCs and compared to the recently demonstrated hybrid materials using bismuth instead of antimony. The hybrid compound is solution-processed onto the photoactive layer based on a classical blend, which is composed of a PTB7-Th low band gap polymer as the donor mixed with PCBM fullerene as the acceptor material.

Durability of Polymer Metal Multilayer: Focus on the Adhesive Chemical Degradation.

Mechanical toughness and high barriers to air and water may be combined in a polymer-metal multilayer film, provided that the two materials are properly bonded together. Delamination is indeed the most severe flaw observed in service. This suggests that the polyurethane (PU) adhesive at the polymer-metal interface fails to bear the shear forces, as happens principally if a multilayer system is submitted to elevated temperature and humidity.

Mechanical Reliability of Flexible Encapsulated Organic Solar Cells: Characterization and Improvement.

The encapsulation of organic photovoltaic (OPV) devices can help mitigate the degradation induced by environmental factors like water and oxygen and thus potential to increase OPV lifetime. Because flexibility is an important parameter for targeted OPV applications, this paper proposes a fundamental study on the impact of the roll-to-roll flexible encapsulation process. Both performance and mechanical reliability of encapsulated devices have been scouted.

Electrical Mapping of Silver Nanowire Networks: A Versatile Tool for Imaging Network Homogeneity and Degradation Dynamics during Failure.

Electrical stability and homogeneity of silver nanowire (AgNW) networks are critical assets for increasing their robustness and reliability when integrated as transparent electrodes in devices. Our ability to distinguish defects, inhomogeneities, or inactive areas at the scale of the entire network is therefore a critical issue. We propose one-probe electrical mapping (1P-mapping) as a specific simple tool to study the electrical distribution in these discrete structures.

Water Vapor Sorption Properties of Polyethylene Terephthalate over a Wide Range of Humidity and Temperature.

The dynamic and equilibrium water vapor sorption properties of amorphous polyethylene terephthalate were determined via gravimetric analysis over a wide range of temperatures (23-70 °C) and humidities (0-90% RH). At low temperature and relative humidity, the dynamics of the sorption process was Fickian. Increasing the temperature or relative humidity induced a distinct up-swing effect, which was associated with a plasticization/clustering phenomenon.