Synthesis and characterization of colloidal ternary ZnCdSe semiconductor nanorods.

For the synthesis of colloidal ternary ZnCdSe nanorods, CdSe nanorods were first prepared under a mixture of tetradecylphosphonic acid/trioctylphosphine oxide surfactants at 250 degrees C, and then ZnSe shell layer was grown onto CdSe nanorods at 180 degrees C, forming CdSeZnSe core/shell nanorods. Green-yellow emitting ternary ZnCdSe nanorods were obtained by a subsequent alloying process at 270 degrees C for 1-3 h through the diffusion of Zn ions into CdSe nanorods. The photoluminescence quantum yield (QY) of ZnCdSe nanorods was 5%-10%, which is higher than that from pristine CdSe nanorods (0.