Ru@hyperbranched Polymer for Hydrogenation of Levulinic Acid to Gamma-Valerolactone: The Role of the Catalyst Support.

Hydrogenation of levulinic acid (LA) obtained from cellulose biomass is a promising path for production of γ-valerolactone (GVL)-a component of biofuel. In this work, we developed Ru nanoparticle containing nanocomposites based on hyperbranched pyridylphenylene polymer, serving as multiligand and stabilizing matrix. The functionalization of the nanocomposite with sulfuric acid significantly enhances the activity of the catalyst in the selective hydrogenation of LA to GVL and allows the reaction to proceed under mild reaction conditions (100 °C, 2 MPa of H) in water and low catalyst loading (0.

Mono- and Bimetallic Nanoparticles Stabilized by an Aromatic Polymeric Network for a Suzuki Cross-Coupling Reaction.

This work addresses the Suzuki cross-coupling between 4-bromoanisole (BrAn) and phenylboronic acid (PBA) in an environmentally benign ethanol-water solvent catalysed by mono- (Pd) and bimetallic (PdAu, PdCu, PdZn) nanoparticles (NPs) stabilised within hyper-cross-linked polystyrene (HPS) bearing tertiary amino groups. Small Pd NPs of about 2 nm in diameters were formed and stabilized by HPS independently in the presence of other metals. High catalytic activity and complete conversion of BrAn was attained at low Pd loading.

Hyper-Cross-Linked Polystyrene as a Stabilizing Medium for Small Metal Clusters.

Among different polymers nanostructured cross-linked aromatics have the greatest potential as catalytic supports due to their exceptional thermal and chemical stability and preservation of the active phase morphology. This work studies the ability of hyper-cross-linked polystyrene (HPS) to stabilize small Pd and Pt ( = 4 or 9) clusters. Unrestricted DFT calculations were carried out for benzene (BZ) adsorption at the BP level of theory using triple-zeta basis sets.

Chitosan as capping agent in a robust one-pot procedure for a magnetic catalyst synthesis.

Here, we report a one-pot solvothermal method for the development of magnetically recoverable catalysts with Ru or Ag nanoparticles (NPs) capped by chitosan (CS), a derivative of natural chitin. The formation of iron oxide NPs was carried out in situ in the presence of CS and iron acetylacetonate in boiling triethyleneglycol (TEG) due to CS solubilization in warm TEG. Coordination with Ru or Ag species and the NP formation take place in the same reaction solution, eliminating intermediate steps.

Pd Catalyst Based on Hyperbranched Polypyridylphenylene Formed In Situ on Magnetic Silica Allows for Excellent Performance in Suzuki-Miyaura Reaction.

Here, for the first time, we developed a catalytic composite by forming a thin layer of a cross-linked hyperbranched pyridylphenylene polymer (PPP) on the surface of mesoporous magnetic silica (FeO-SiO, MS) followed by complexation with Pd species. The interaction of Pd acetate (PdAc) with pyridine units of the polymer results in the formation of Pd complexes which are evenly distributed through the PPP layer. The MS-PPP-PdAc catalyst was tested in the Suzuki-Miyaura cross-coupling reaction with four different para-Br-substituted arenes, demonstrating enhanced catalytic properties for substrates containing electron withdrawing groups, and especially, for 4-bromobenzaldehyde.

Fabrication of magnetically recoverable catalysts based on mixtures of Pd and iron oxide nanoparticles for hydrogenation of alkyne alcohols.

We report a novel method for development of magnetically recoverable catalysts prepared by thermal decomposition of palladium acetylacetonate in the presence of iron oxide nanoparticles (NPs). Depending on conditions, the reaction results either in a dispersed mixture of Pd and iron oxide NPs or in their aggregates. It was demonstrated that the Pd loading, reaction temperature, solvent, and iron oxide NP size and composition are crucial to control the reaction product including the degree of aggregation of Pd and iron oxide NPs, and the catalyst properties.

γ-Fe₂O₃ nanoparticle surface controls PtFe nanoparticle growth and catalytic properties.

We report a novel method for synthesis of alloy PtFe nanoparticles (NPs) of different compositions using γ-Fe2O3 NPs as an iron source. We show here other growth mechanisms than conventional nucleation on a NP surface leading to core-shell NP or seeded NP growth. Depending on reaction conditions, different compositions of PtFe NPs can be obtained.

Functionalization of monodisperse iron oxide NPs and their properties as magnetically recoverable catalysts.

Here we report the functionalization of monodisperse iron oxide nanoparticles (NPs) with commercially available functional acids containing multiple double bonds such as linolenic (LLA) and linoleic (LEA) acids or pyridine moieties such as 6-methylpyridine-2-carboxylic acid, isonicotinic acid, 3-hydroxypicolinic acid, and 6-(1-piperidinyl)pyridine-3-carboxlic acid (PPCA). Both double bonds and pyridine groups can be reacted with noble metal compounds to form catalytically active species in the exterior of magnetic NPs, thus making them promising magnetically recoverable catalysts. We determined that both LLA and LEA stabilize magnetic iron oxide NPs, allowing the formation of π-complexes with bis(acetonitrile)dichloropalladium(II) in the NP shells.