Solvothermal Synthesis of Hierarchical TiO Microstructures with High Crystallinity and Superior Light Scattering for High-Performance Dye-Sensitized Solar Cells.

In this article, hierarchical TiO microstructures (HM-TiO) were synthesized by a simple solvothermal method adopting tetra-n-butyl titanate as the titanium source in a mixed solvent composed of N,N-dimethylformamide and acetic acid. Due to the high crystallinity and superior light-scattering ability, the resultant HM-TiO are advantageous as photoanodes for dye-sensitized solar cells. When assembled to the entire photovoltaic device with C101 dye as a sensitizer, the pure HM-TiO-based solar cells showed an ultrahigh photovoltage up to 0.

Fine Tuning of Nanocrystal and Pore Sizes of TiO2 Submicrospheres toward High Performance Dye-Sensitized Solar Cells.

In general, the properties and performance of mesoporous TiO2 are greatly dependent on its crystal size, crystallinity, porosity, surface area, and morphology; in this regard, design and fine-tuning the crystal and pore sizes of the TiO2 submicrospheres and investigating the effect of these factors on the properties and photoelectric performance of dye-sensitized solar cells (DSSCs) is essential. In this work, uniform TiO2 submicrospheres were synthesized by a two-step procedure containing hydrolysis and solvothermal process. The crystal and pore sizes of the TiO2 submicrospheres were fine-tuned and controlled in a narrow range by adjusting the quantity of NH4OH during the solvothermal process.

Mesoporous TiO2 Yolk-Shell Microspheres for Dye-sensitized Solar Cells with a High Efficiency Exceeding 11%.

Yolk-shell TiO2 microspheres were synthesized via a one-pot template-free solvothermal method building on the aldol condensation reaction of acetylacetone. This unique structure shows superior light scattering ability resulting in power conversion efficiency as high as 11%. This work provided a new synthesis system for TiO2 microspheres from solid to hollow and a novel material platform for high performance solar cells.

One-Pot Synthesis of Mesoporous TiO₂ Micropheres and Its Application for High-Efficiency Dye-Sensitized Solar Cells.

TiO2 microspheres are of great interest for a great deal of applications, especially in the solar cell field. Because of their unique microstructure and light-scattering effect, TiO2 microsphere-based solar cells often exhibit superior photovoltaic performance. Hence, exploring new suitable TiO2 microspheres for high-efficiency solar cells is essential.

[In situ diffuse reflectance FTIR spectroscopy study of CO adsorption on Ni2P/mesoporous molecule sieve catalysts].

Abstract The supported nickel phosphate precursors were prepared by incipient wetness impregnation using nickel nitrate as nickel source, diammonium hydrogen phosphate as phosphorus source, and MCM-41, MCM-48, SBA-15 and SBA-16 as supports, respectively. Then, the supported Ni2 P catalysts were prepared by temperature-programmed reduction in flowing Hz from their nickel phosphate precursors. The in situ diffuse reflectance FTIR spectroscopy (DRIFTS) analysis with the probe molecule CO was carried out to characterize the surface properties.