Estimation of shelf life of natural rubber latex exam-gloves based on creep behavior.

Samples of full-length glove-fingers cut from chlorinated and nonchlorinated latex medical examination gloves were aged for various times at several fixed temperatures and 25% relative humidity. Creep testing was performed using an applied stress of 50 kPa on rectangular specimens (10 mm x 8 mm) of aged and unaged glove fingers as an assessment of glove loosening during usage. Variations in creep curves obtained were compared to determine the threshold aging time when the amount of creep became larger than the initial value.

An in vitro study of the effect of in-folds on the durability of mammary implants.

We hypothesize that the presence of in-folding in a filled mammary shell leads to shortening of the time to failure under tensile fatigue. Specimens, cut from pristine shells, were mounted in S-folded, creased, and unfolded configurations. A characteristic change, occurring in a transmembrane capacitance-proportional alternating current (AC) signal, which was used to monitor working of each specimen, was chosen as a robust marker that preceded frank shell perforation.