Electrochemical and in vitro biological behaviors of a Ti-Mo-Fe alloy specifically designed for stent applications.

There is a deep interest in developing new Ni-free Ti-based alloys to replace 316 L stainless steel and Co-Cr alloys for endovascular stent application, mainly because the release of Ni can generate toxicity and allergenicity. Interactions of Ti alloy biomaterials with bone cells and tissues have been widely investigated and reported, while interactions with vascular cells and tissues, such as endothelial cells (ECs) and smooth muscle cells (SMCs), are scarce. Therefore, this study focused on the relationship among the surface finishing features, corrosion behavior and in vitro biological performances regarding human ECs, SMCs and blood of a newly developed Ti-8Mo-2Fe (TMF) alloy, specifically designed for balloon-expandable stent applications.

Effect of an amorphous titania nanotubes coating on the fatigue and corrosion behaviors of the biomedical Ti-6Al-4V and Ti-6Al-7Nb alloys.

An array of self-organized TiO nanotubes with an amorphous structure was produced on the biomedical Ti-6Al-4V and Ti-6Al-7Nb alloys, and the resulting fatigue and corrosion behaviors were studied. The electrochemical response of the nanotubular oxide surfaces was investigated in Ringer physiological solution through potentiodynamic polarization and electrochemical impedance spectroscopy measurements. The absence of transpassivation in the chloride-containing solution, in addition to the micron-scale values of the passivation current density, indicated the excellent corrosion behavior of the coating and the satisfactory protection against the creation of potential stress concentrators in the surface.

Fatigue behavior of Ti-6Al-4V alloy in saline solution with the surface modified at a micro- and nanoscale by chemical treatment.

This work evaluated the influence of the surface modification using acid etching combined with alkaline treatment on the fatigue strength of Ti-6Al-4V ELI alloy. The topography developed by chemical surface treatments (CST) was examined by scanning electron microscopy (SEM) and confocal laser scanning microscopy (CLSM). Increased roughness and effective surface area were investigated and compared with the Ti-6Al-4V samples without modification.