Nanofibrous material from hyaluronan derivatives preserving fibrous structure in aqueous environment.

Nanofibrous materials produced from natural polymers have wide range of potential uses in regenerative medicine. This paper focuses on preparation of nanofibrous layers produced from intentionally hydrophobized derivatives of hyaluronan, which is known for its ability to promote wound healing. This structural modification of hyaluronan expands the range of potential uses of this promising material, which is otherwise limited due to the hydrophilic nature of hyaluronic acid.

Effects of emulsion, dispersion, and blend electrospinning on hyaluronic acid nanofibers with incorporated antiseptics.

Nanofibrous materials are used in drug delivery as carriers of active ingredients. These can be incorporated into the materials with various electrospinning methods that differ mainly in the way spinning solutions are prepared. Each method affects primarily the encapsulation efficiency and distribution of active ingredients in the materials.

Antimicrobial nanofibrous mats with controllable drug release produced from hydrophobized hyaluronan.

Due to their large active surface, high loading efficiency, and tunable dissolution profiles, nanofibrous mats are often cited as promising drug carriers or antimicrobial membranes. Hyaluronic acid has outstanding biocompatibility, but it is hydrophilic. Nanofibrous structures made from hyaluronan dissolve immediately, making them unsuitable for controlled drug release and longer applications.

Electrospinning of Fibrous Layers Containing an Antibacterial Chlorhexidine/Kaolinite Composite.

The aim of this study was to prepare self-supporting homogeneous nano/microfibrous layers with a content of the clay mineral kaolinite and kaolinite modified with the antibacterial agent chlorhexidine (CH). Fibers were made of hydrophobic polymers-polyurethane and polycaprolactone. Polymer suspensions for electrospinning contained 2, 5, and 8 wt % (relative to the total weight of the suspension) of kaolinite or CH/kaolinite and were electrospun using 4SPIN LAB.