Evaluation of the Microstructure and Mechanical Properties of the Butt-Welded Joints of Spiral Pipes Made of L485ME (X70) Steel.

The expansion of the gas pipeline network makes it necessary, on the one hand, to meet the requirements of standards regarding the materials used, but on the other hand, it is necessary to weld them. In the case of natural gas as a fuel, the welding process is widely used, but in the case of replacing natural gas with a mixture of this gas and hydrogen, the requirements regarding the quality of the process must be significantly increased or the process must be completely changed. This article presents the results of testing welded joints for a newly developed welding technology for the transmission of a hydrogen mixture.

Effect of Post-Weld Heat Treatment on Microstructure and Hardness of Laser Beam Welded 17-4 PH Stainless Steel.

This article presents the results of research on the development of the technology of laser beam butt welding of 17-4 PH stainless steel sheets and the technology of post-weld heat treatment (PWHT). The developed technology allows for favorable conditions to be obtained and for the appropriate microstructure and hardness to exist in the weld area. Moreover, it enables the fulfillment of a number of specific requirements beyond the possibilities of manual welding and other methods.

Effect of Multi-Variant Thermal Treatment on Microstructure Evolution and Mechanical Properties of AlSi10Mg Processed by Direct Metal Laser Sintering and Casting.

This article presents a study on the influence of temperature and time of multi-variant heat treatment on the structure and properties of materials produced in direct metal laser sintering (DMLS) and casting technology. The materials were manufactured in the form of cuboidal elements with a cross-section of 1.5 mm × 15 mm and a length of 60 mm.

Analysis of Microstructure and Mechanical Properties of AlSi11 after Chip Recycling, Co-Extrusion, and Arc Welding.

Recycling of raw materials and is crucial for the production of new products for the global economy. The aim here is, on the one hand, to reduce energy consumption, and, on the other hand, to obtain materials with similar functional properties. The study undertook research on the possibility of processing AlSi11 aluminum chips by compaction and co-extruding to obtain a product in the form of a flat bar with mechanical properties not lower than those of the cast materials.

Analysis of the Possibility of Plastic Deformation Characterisation in X2CrNi18-9 Steel Using Measurements of Electromagnetic Parameters.

An analysis was conducted on the possibility of making an assessment of the degree of plastic deformation ε in X2CrNi18-9 steel by measuring three electromagnetic diagnostic signals: the Barkhausen noise features, the impedance components in in-series LCR circuits, and the residual magnetic field components. The impact of ε on a series of different extracted features of diagnostic signals was investigated. The occurrence of two regions of sensitivity was found for all the features of the analysed signals.

Influence of the Thermal Cutting Process on Cracking of Pearlitic Steels.

The paper presents research results of the influence of heat input into high carbon rail steel during cutting processes on microstructure transformation and cracking. The massive block of steel prepared for rail rolling processes was cut and examined by nondestructive magnetic testing and destructive testing by microscopic examination and hardness measurements. The results show unfavorable microstructure changes where pearlite and transformed ledeburite were obtained.