Compression Molding of Low-Density Polyethylene Matrix/Glass-Fiber-Reinforced Thick Laminates.

Thermoplastic fiberglass was compression molded in the form of thick panels with a nominal thickness of 10 mm and a size of 300 × 300 mm. A simplified procedure was adopted to speed up the lamination procedure and adapt it to the aim of recycling waste, glass fibers, fabrics, and thermoplastic films. Low density polyethylene was used as a matrix to simplify the laboratory process, but the same procedure can be extended to other thermoplastic film, such as polyamide.

Shape Memory Composite Sandwich Structures with Self-Healing Properties.

In this study, Polyurea/Formaldehyde (PUF) microcapsules containing Dicyclopentadiene (DCPD) as a healing substance were fabricated in situ and mixed at relatively low concentrations (<2 wt%) with a thermosetting polyurethane (PU) foam used in turn as the core of a sandwich structure. The shape memory (SM) effect depended on the combination of the behavior of the PU foam core and the shape memory polymer composite (SMPC) laminate skins. SMPC laminates were manufactured by moulding commercial carbon fiber-reinforced (CFR) prepregs with a SM polymer interlayer.