Elastic Properties of Polychloroprene Rubbers in Tension and Compression during Ageing.

Being able to predict the lifetime of elastomers is fundamental for many industrial applications. The evolution of both tensile and compression behavior of unfilled and filled neoprene rubbers was studied over time for different ageing conditions (70 °C, 80 °C and 90 °C). While Young's modulus increased with ageing, the bulk modulus remained almost constant, leading to a slight decrease in the Poisson's ratio with ageing, especially for the filled rubbers.

Loaded Ce-Ag organic-inorganic hybrids and their antibacterial activity.

There are requirements for surfaces with antibacterial properties in various technological fields. U-PEO hybrids with antibacterial properties were synthesized by the sol-gel process, incorporating combinations of cerium and silver salts at different silver molar fractions (0, 0.02, 0.

Synthesis and characterization of Fe doped CeO2 nanoparticles for pigmented ultraviolet filter applications.

Iron doped CeO2 nanoparticles with doping concentrations between 0 and 30 mol% were synthesized by the co-precipitation method for potential application as a pigmented ultraviolet filtration material. Each sample was calcined in air and in argon. The iron solubility limit in the CeO2 lattice was found to be between 10 and 20 mol%.

Synthesis of nano-hematite for possible use in sunscreens.

Hematite nanoparticles were synthesized for ultraviolet filtration application by the precipitation method followed by calcination at different temperatures. A range of crystallite sizes between 37 and 85 nm (as determined by the Scherrer formula) was obtained, according to the temperature used for the calcination. An increase in the absorbance with increasing crystallite size was observed over the whole ultraviolet B and A range.