Reorientation of Suspended Ceramic Particles in Robocasted Green Filaments during Drying.

This work considers the fabrication of ceramic parts with the help of an additive manufacturing process, robocasting, in which a paste with suspended particles is robotically extruded. Within the final part, the material properties depend on the orientation of the particles. A prediction of the particle orientation is challenging as the part usually undergoes multiple processing steps with varying contributions to the orientation.

Microstructural Analysis of Novel Preceramic Paper-Derived SiC/SiC Composites.

This paper presents the results of microstructural analysis of novel preceramic paper-derived SiCf/SiC composites fabricated by spark plasma sintering. The sintering temperature and pressure were 2100/2200 °C and 60/100 MPa, respectively. The content of fibers in the composites was approx.

Optimization and Characterization of Preceramic Inks for Direct Ink Writing of Ceramic Matrix Composite Structures.

In a previous work, an ink based on a preceramic polymer, SiC fillers, and chopped carbon fibers was proposed for the production of Ceramic Matrix Composite (CMC) structures by Direct Ink Writing (DIW) and subsequent pyrolysis. Thanks to the shear stresses generated at the nozzle tip during extrusion, carbon fibers can be aligned along the printing direction. Fumed silica was added to the ink in order to enhance its rheological properties; however, the printed structures still showed some deformation in the Z direction.