Magnetodielectric and Rheological Effects in Magnetorheological Suspensions Based on Lard, Gelatin and Carbonyl Iron Microparticles.

This study aims to develop low-cost, eco-friendly, and circular economy-compliant composite materials by creating three types of magnetorheological suspensions (MRSs) utilizing lard, carbonyl iron (CI) microparticles, and varying quantities of gelatin particles (GP). These MRSs serve as dielectric materials in cylindrical cells used to fabricate electric capacitors. The equivalent electrical capacitance () of these capacitors is measured under different magnetic flux densities (B≤160 mT) superimposed on a medium-frequency electric field ( = 1 kHz) over a period of 120 s.

A Cotton Fabric Composite with Light Mineral Oil and Magnetite Nanoparticles: Effects of a Magnetic Field and Uniform Compressions on Electrical Conductivity.

Over the past few decades, tactile sensors have become an emerging field of research with direct applications in the area of biomedical engineering. New types of tactile sensors, called magneto-tactile sensors, have recently been developed. The aim of our work was to create a low-cost composite whose electrical conductivity depends on mechanical compressions that can be finely tuned using a magnetic field for magneto-tactile sensor fabrication.

Magneto-Tactile Sensor Based on a Commercial Polyurethane Sponge.

In this paper, we present the procedure for fabricating a new magneto-tactile sensor (MTS) based on a low-cost commercial polyurethane sponge, including the experimental test configuration, the experimental process, and a description of the mechanisms that lead to obtaining the MTS and its characteristics. It is shown that by using a polyurethane sponge, microparticles of carbonyl iron, ethanol, and copper foil with electroconductive adhesive, we can obtain a high-performance and low-cost MTS. With the experimental assembly described in this paper, the variation in time of the electrical capacity of the MTS was measured in the presence of a deforming force field, a magnetic field, and a magnetic field superimposed over a deformation field.

Physical Mechanisms of Magnetic Field Effects on the Dielectric Function of Hybrid Magnetorheological Suspensions.

In this paper, we study the electrical properties of new hybrid magnetorheological suspensions (hMRSs) and propose a theoretical model to explain the dependence of the electric capacitance on the iron volumetric fraction, ΦFe, of the dopants and on the external magnetic field. The hMRSs, with dimensions of 30 mm×30 mm×2 mm, were manufactured based on impregnating cotton fabric, during heating, with three solutions of iron microparticles in silicone oil. Flat capacitors based on these hMRSs were then produced.

Electrical and Magnetodielectric Properties of Magneto-Active Fabrics for Electromagnetic Shielding and Health Monitoring.

An efficient, low-cost and environmental-friendly method to fabricate magneto-active fabrics (MAFs) based on cotton fibers soaked with silicone oil and iron oxide microfibers (mFe) at mass fractions 2 wt.%, 4 wt.% and 8 wt.