Synthesis and assembly of gold nanoparticle-doped polymer solid foam films at the liquid/liquid interface and their catalytic properties.

Gold nanoparticle-doped poly(2-vinylpyridine) (P2VP) microcapsules and foam films were synthesized and assembled at the P2VP chloroform solution/HAuCl(4) aqueous solution interface at 25 °C. It was found that Au nanoparticles with the average diameter of 2.1 nm were homogeneously embedded in and adsorbed on the walls of the capsules and foams, the nanoparticles were composed of Au(0) and Au(III) with the molar ratio of about 75/25, and the mass percent of Au elements was measured to be 19.

One-step synthesis and assembly of two-dimensional arrays of mercury sulfide nanocrystal aggregates at the air/water interface.

Ordered two-dimensional (2D) arrays of β-HgS nanocrystal aggregates were prepared successfully at the air/water interface through the interfacial reaction between Hg(2+) ions in the subphase and H(2)S in the gaseous phase under the direction of liquid-expanded monolayers of arachidic acid (AA). These 2D arrays are composed of hexagonal or quasi-hexagonal aggregates with the size of several hundreds of nanometers that consist of several tens of HgS nanocrystals with the size of several nanometers. The formed HgS nanocrystals together with AA molecules self-assembled into round aggregates due to the interactions between the species, and the aggregates self-assembled into 2D arrays further due to the attractions between them.