Fretting and corrosion of metal liners from modular dual mobility constructs : a retrieval analysis.

Aims: Dual mobility implants in total hip arthroplasty are designed to increase the functional head size, thus decreasing the potential for dislocation. Modular dual mobility (MDM) implants incorporate a metal liner (e.g.

Zirconia Phase Transformation in Zirconia-Toughened Alumina Ceramic Femoral Heads: An Implant Retrieval Analysis.

Background: Zirconia-toughened alumina ceramic was introduced as a femoral head material for total hip arthroplasty. The material combines the stability of alumina with the toughness of zirconia. Despite inherent benefits for bearing surfaces, concern exists in the medical field that phase transformation of the zirconia grains could worsen wear resistance and lower the strength of the head.

Do oxidized zirconium heads decrease tribocorrosion in total hip arthroplasty? A study of retrieved components.

Aims: The aim of this study was to evaluate fretting and corrosion in retrieved oxidized zirconium (OxZr; OXINIUM, Smith & Nephew, Memphis, Tennessee) femoral heads and compare the results with those from a matched cohort of cobalt-chromium (CoCr) femoral heads.

Patients And Methods: A total of 28 OxZr femoral heads were retrieved during revision total hip arthroplasty (THA) and matched to 28 retrieved CoCr heads according to patient demographics. The mean age at index was 56 years (46 to 83) in the OxZr group and 70 years (46 to 92) in the CoCr group.

Distribution of Bone Ongrowth in Metaphyseal Sleeves for Revision Total Knee Arthroplasty: A Retrieval Analysis.

Background: The metaphyseal region of the bone has been recognized by its importance to the overall stability of a revision construct. Porous titanium metaphyseal sleeves to enhance biologic fixation can be used to manage bone loss encountered during revision total knee arthroplasty. While clinical results for metaphyseal sleeves are encouraging, there is little information on the extent to which biologic fixation is achievable with metaphyseal sleeves.

Antioxidant-stabilized highly crosslinked polyethylene in total knee arthroplasty: a retrieval analysis.

Aims: The aim of this study was to evaluate the surface damage, the density of crosslinking, and oxidation in retrieved antioxidant-stabilized highly crosslinked polyethylene (A-XLPE) tibial inserts from total knee arthroplasty (TKA), and to compare the results with a matched cohort of standard remelted highly crosslinked polyethylene (XLPE) inserts.

Materials And Methods: A total of 19 A-XLPE tibial inserts were retrieved during revision TKA and matched to 18 retrieved XLPE inserts according to the demographics of the patients, with a mean length of implantation of 15 months (1 to 42). The percentage areas of PE damage on the articular surfaces and the modes of damage were measured.