Bioresorption and Biomineralization of S53P4 Bioactive Glass in Neutral Tris Buffer and Citric Acid Solution.

In this study, S53P4 (53SiO-23NaO-20CaO-4PO) bioactive glass (BG) were prepared through a melt-milling process, and their bioresorption and biomineralization behavior was evaluated by in vitro dissolution under different solution conditions (neutral and acidic). The particle size of S53P4 BG was controlled by milling, and the in vitro dissolution evaluation was performed in tris buffer and citric acid solution for 21 days at 37 °C according to ISO 10993-14 (biological evaluation of medical devices). During dissolution, the ion release rate of S53P4 BG was confirmed to be three times faster in citric acid solution than that in tris buffer.