Magnetic Polypyrrole-Gelatin-Barium Ferrite Cryogel as an Adsorbent for Chromium (VI) Removal.

Polypyrrole-gelatin aerogels, containing magnetic barium ferrite (BaFe) particles, (PPy-G-BaFe) were synthesized by oxidative cryopolymerization and used as adsorbents for the removal of Cr(VI) from aqueous media. The removal was performed at pH 4, which was shown to be the optimal value, due to HCrO being the dominant species in these conditions and its more favorable adsorption and reduction compared to CrO, present at pH > 4. It was found that the presence of magnetic BaFe particles had no effect on the adsorption performance of PPy aerogels in terms of capacity and kinetics, which was attributed to its relatively low content in the composite.

Effect of a Zr-Based Metal-Organic Framework Structure on the Properties of Its Composite with Polyaniline.

Composites of polyaniline (PANI) and Zr-based metal-organic frameworks (MOFs), UiO-66 and UiO-66-NH, were synthesized by the oxidative polymerization of aniline in the presence of MOF templates with the MOF content in the resulting materials (78.2 and 86.7 wt %, respectively) close to the theoretical value (91.

Polypyrrole-Barium Ferrite Magnetic Cryogels for Water Purification.

Magnetic polypyrrole-gelatin-barium ferrite (PPy-G-BaFe) cryogels/aerogels were synthesized by one-step oxidative cryopolymerization of pyrrole in the presence of various fractions of barium ferrite (BaFe) nanoparticles, dispersed in aqueous gelatin solution. The successful incorporation of BaFe into the composites was confirmed by elemental analysis and scanning electron microscopy paired with an energy-dispersive X-ray detector. The maximum achieved content of BaFe in the resulting material was 3.

Carbon Materials Derived from Poly(aniline---phenylenediamine) Cryogels.

Nitrogen-containing carbon derivatives were prepared by the carbonization of poly(aniline---phenylenediamine) cryogels in inert atmosphere. Lower aniline fraction in the comonomer mixture used for preparation of the cryogels led to the decrease of their thermal stability, a consequent increase of carbonization degree, and less defective structure of carbonized materials. The resulting carbonaceous products had up to 4 orders of magnitude higher specific surface area than their respective cryogel precursors, the highest value 931 m g being achieved for carbonized poly(-phenylenediamine) cryogel.