Chemical Bath Deposition of p-Type Transparent, Highly Conducting (CuS)x:(ZnS)1-x Nanocomposite Thin Films and Fabrication of Si Heterojunction Solar Cells.

P-type transparent conducting films of nanocrystalline (CuS)x:(ZnS)1-x were synthesized by facile and low-cost chemical bath deposition. Wide angle X-ray scattering (WAXS) and high resolution transmission electron microscopy (HRTEM) were used to evaluate the nanocomposite structure, which consists of sub-5 nm crystallites of sphalerite ZnS and covellite CuS. Film transparency can be controlled by tuning the size of the nanocrystallites, which is achieved by adjusting the concentration of the complexing agent during growth; optimal films have optical transmission above 70% in the visible range of the spectrum.

Antimony Doping in Solution-processed Cu2 ZnSn(S,Se)4 Solar Cells.

Kesterite Cu2 ZnSn(S,Se)4 (CZTSSe) is obtained using a facile precursor-solution method followed by selenization. Power-conversion efficiency of 6.0 % is achieved and further improved to 8.

Uncovering loss mechanisms in silver nanoparticle-blended plasmonic organic solar cells.

There has been much controversy over the incorporation of organic-ligand-encapsulated plasmonic nanoparticles in the active layer of bulk heterojunction organic solar cells, where both enhancement and detraction in performance have been reported. Here through comprehensive transient optical spectroscopy and electrical characterization, we demonstrate evidence of traps responsible for performance degradation in plasmonic organic solar cells fabricated with oleylamine-capped silver nanoparticles blended in the poly (3-hexylthiophene):[6,6]-phenyl-C 61-butyric acid methyl ester active layer. Despite an initial increase in exciton generation promoted by the presence of silver nanoparticles, transient absorption spectroscopy reveals no increase in the later free polaron population-attributed to fast trapping of polarons by nearby nanoparticles.