Mechanical properties of glass-ceramic A-W-polyethylene composites: effect of filler content and particle size.

Composites which comprise a bioactive filler and ductile polymer matrix are desirable as implant materials since both their biological and mechanical properties can be tailored for a given application. In the present study three-point bending was used to characterise biomedical materials composed of glass-ceramic apatite-wollastonite (A-W) particulate reinforced polyethylene (PE) (denoted as AWPEX). The effects of filler volume fraction, varied from 10 to 50 vol%, and average particle size, 4.

Bonding strength of the apatite layer formed on glass-ceramic apatite-wollastonite-polyethylene composites.

Bioactive glass-ceramic apatite-wollastonite (A-W) has been incorporated into polyethylene in particulate form to create new bioactive composites for potential maxillofacial applications. The effects of varying the volume fraction of glass-ceramic A-W filler and the glass-ceramic A-W particle size were investigated by measuring the bonding strength of the bonelike apatite layer formed on the surface of glass-ceramic A-W-polyethylene composites. The bonding strength was evaluated via a modified ASTM C-333 standard in which a tensile stress was applied to the substrate and the strength of the bioactive layer was compared with that formed on commercially available hydroxyapatite-polyethylene composite samples, HAPEX.

Osteoinduction of porous bioactive titanium metal.

This is the first report of bone induction in a non-osseous site by titanium metal, which has long been recognized as a non-bioactive material. After undergoing specific chemical and thermal treatments, porous bioactive titanium induced bone formation without the need of additional osteogenic cells or osteoinductive agents. Four types of titanium implants were implanted in the dorsal muscles of mature beagle dogs, and were examined histologically after periods of 3 and 12 months.

Apatite-forming ability and mechanical properties of PTMO-modified CaO-SiO2-TiO2 hybrids derived from sol-gel processing.

Hydrolysis and polycondensation of triethoxysilane end-capped Poly (tetramethylene oxide) (Si-PTMO), tetraethoxysilane (TEOS), tetraisopropyltitanate (TiPT) and calcium nitrate (Ca(NO(3))(2)) gave transparent monolithics of PTMO-modified CaO-SiO(2)-TiO(2) hybrids. The samples with (TiPT)/(TEOS+TiPT) molar ratios from 0 to 0.20 under constant ratio of (Si-PTMO)/(TEOS+TiPT) of 2/3 in weight were prepared.

Histological and mechanical investigation of the bone-bonding ability of anodically oxidized titanium in rabbits.

The purpose of this study was to histologically and mechanically investigate the in vivo bone-bonding ability of anodically oxidized titanium (AO Ti) with an anatase crystal layer on its surface. AO Ti plates, anodically oxidized at 155 V in 1 M H2SO4, were implanted into the proximal metaphyses of mature rabbit tibiae for 4, 8, 16, and 24 weeks and investigated by light microscopy, scanning electron microscopy and detaching test. High bone-bonding ability, comparable to our previous study data of the bioactive titanium produced by sodium-free alkali and heat treatment, was observed at the early stages of implantation.

Promoter-specific function of the TATA element in undifferentiated P19 cells.

P19 embryonal carcinoma cells differentiate into neuronal cells when treated with retinoic acid (RA). To explore the importance of core promoter structures in the regulation of gene expression during neuronal differentiation, the activities of three classes of modified or unmodified model promoters (Spec2a, OtxE, and Ars) were compared in P19 cells before and after RA treatment. The Spec2a promoter was activated in undifferentiated cells specifically when the E-box was located at a proximal position, whereas the OtxE promoter was activated when the E-box was in a distal position.

Phase stability after aging and its influence on pin-on-disk wear properties of Ce-TZP/Al2O3 nanocomposite and conventional Y-TZP.

Recently zirconia/alumina composites have been examined by many researchers as the new generation of bearing materials in total joint replacements. In this study, the phase stability of a Ce-TZP/Al(2)O(3) nanocomposite and conventional Y-TZP after aging, and its influence on wear resistance, were investigated. Very slight phase transformation was observed in both types of ceramics 18 months after the implantation of Ce-TZP/Al(2)O(3) or Y-TZP samples into rabbit tibiae.

Biology of alkali- and heat-treated titanium implants.

In cementless fixation systems, surface character is an important factor. Alkali and heat treatments of titanium metal have been shown to produce strong bonding to bone and a higher ongrowth rate. In this study we examined the effect of alkali and heat treatments on titanium rods in an intramedullary rabbit femur model, in regard to the cementless hip stem.

Identification of a novel TATA element-binding protein binding region at the N terminus of the Saccharomyces cerevisiae TAF1 protein.

TFIID, a multiprotein complex composed of TATA element-binding protein (TBP) and 14 TBP-associated factors (TAFs), can directly recognize core promoter elements and mediate transcriptional activation. The TAF N-terminal domain (TAND) of TAF1 may play a significant role in these two principal TFIID functions by regulating the access of TBP to the TATA element. In yeast, TAND consists of two subdomains, TAND1 (10-37 amino acids (aa)) and TAND2 (46-71 aa), which interact with the concave and convex surfaces of TBP, respectively.

Preparation of antibacterial silver-doped silica glass microspheres.

Various types of inorganic substances doped with silver ions have been developed as antibacterial materials, and some have already been commercialized. Colorless and chemically durable materials that slowly release silver ions are, however, still need to be developed. The present authors have previously shown that when a silica glass doped with silver and aluminium ions is prepared using the sol-gel method, the resultant product is colorless, chemically durable, and slowly releases silver ions into water over a long period.

Repair of segmental long bone defect in rabbit femur using bioactive titanium cylindrical mesh cage.

A segmental rabbit femur defect was repaired using an empty bioactive titanium (BAT) mesh cage. A 10mm long titanium mesh cage was positioned in the bony defect and reinforced by intramedullary fixation. The BAT surface was prepared by chemical and thermal treatment.

Effect of particle size on zinc release from zinc containing tricalcium phosphate (ZnTCP) in Zn-deficient osteoporosis rats.

The effect of particle size on in vivo and in vitro Zn release of ZnTCP was investigated for the purpose of understanding Zn release behavior from a sustained-release device. The tricalcium phosphate powders (Ca2.7 Zn0.

The orally available spleen tyrosine kinase inhibitor 2-[7-(3,4-dimethoxyphenyl)-imidazo[1,2-c]pyrimidin-5-ylamino]nicotinamide dihydrochloride (BAY 61-3606) blocks antigen-induced airway inflammation in rodents.

Spleen tyrosine kinase (Syk) tyrosine kinase plays essential roles in receptors for Fc portion of immunoglobulins and B cell receptor complex signaling in various inflammatory cells; therefore, inhibitors of Syk kinase may show potential as antiasthmatic/allergic therapeutics. We identified 2-[7-(3,4-dimethoxyphenyl)-imidazo[1,2-c]pyrimidin-5-ylamino]-nicotinamide dihydrochloride (BAY 61-3606), a potent (Ki = 7.5 nM) and selective inhibitor of Syk kinase.

Thromboresistance of alkali- and heat-treated titanium metal formed with apatite.

Fibrin deposition and platelet adhesion onto alkali- and heat-treated titanium metal (AH-Ti), alkali- and water-treated titanium metal (Wa-Ti), and alkali- and heat-treated titanium metal formed with apatite (Ap-Ti) in simulated body fluid (SBF) were evaluated by exposure to anticoagulated blood or washed platelet suspension (WPS) under static conditions and subsequent observation with scanning electron microscopy (SEM). The results were compared with those for commercially pure titanium metal (cp-Ti). Thrombus formation on AH-Ti and Wa-Ti, which were exposed to heparinized whole blood for 1 h, was significantly less than that on cp-Ti, on which pronounced depositions of fibrin-erythrocytes and lymphocytes were observed.

Preparation of ceramic microspheres for in situ radiotherapy of deep-seated cancer.

Radiotherapy is one of the most effective treatments for cancers. However, external irradiation provides only small doses to deep-seated cancers, and often causes damage to healthy tissues. It has been reported that 20-30 microm diameter 17Y(2)O(3)-19Al(2)O(3)-64SiO(2) (mol%) glass microspheres are useful for the in situ irradiation of cancers.

Preparation and assessment of revised simulated body fluids.

A simulated body fluid (SBF) with ion concentrations approximately equal to those of human blood plasma has been used widely for in vitro assessment of the bioactivity of artificial materials and for the formation of bone-like apatite on various substrates. The ion concentrations of a conventional SBF (c-SBF) are, however, not exactly equal to those of blood plasma. In the present study, a revision of c-SBF was made to prepare new SBFs (r-SBF, i-SBF, and m-SBF) with ion concentrations equal to or closer to those of blood plasma.

Novel bioactive materials with different mechanical properties.

Some ceramics, such as Bioglass, sintered hydroxyapatite, and glass-ceramic A-W, spontaneously bond to living bone. They are called bioactive materials and are already clinically used as important bone substitutes. However, compared with human cortical bone, they have lower fracture toughness and higher elastic moduli.

Apatite-forming ability of carboxyl group-containing polymer gels in a simulated body fluid.

Carboxymethylated chitin, gellan gum, and curdlan gels were soaked in a simulated body fluid (SBF) having ion concentrations nearly equal to those of human blood plasma. Some of the gels had been soaked in a saturated Ca(OH)(2) solution, while others had not. The carboxymethylated chitin and gellan gum gels have carboxyl groups, while the curdlan gel has hydroxyl groups.

PMMA-based bioactive cement: effect of CaF2 on osteoconductivity and histological change with time.

A new bioactive bone cement (designated GBC), which is a polymethyl methacrylate- (PMMA-) based composite consisting of bioactive glass beads as an inorganic filler and high-molecular-weight PMMA (hPMMA) as an organic matrix, has been developed. The bioactive glass beads consist of MgO-CaO-SiO(2)-P(2)O(5)-CaF(2) glass. The purpose of the present study was to evaluate the effect of CaF(2) on osteoconductivity and to evaluate the degree of cement degradation with time.

Bonelike apatite formation on ethylene-vinyl alcohol copolymer modified with silane coupling agent and calcium silicate solutions.

An ethylene-vinyl alcohol copolymer (EVOH) was treated with a silane coupling agent and calcium silicate solutions, and then soaked in a simulated body fluid (SBF) with ion concentrations approximately equal to those of human blood plasma. A smooth and uniform bonelike apatite layer was successfully formed on both the EVOH plate and the EVOH-knitted fibers in SBF within 2 days. Part of the structure of the resulting apatite-EVOH fiber composite was similar to that of natural bone.

Mutations in the histone fold domain of the TAF12 gene show synthetic lethality with the TAF1 gene lacking the TAF N-terminal domain (TAND) by different mechanisms from those in the SPT15 gene encoding the TATA box-binding protein (TBP).

The general transcription factor TFIID, composed of the TATA box-binding protein (TBP) and 14 TBP-associated factors (TAFs), is important for both basal and regulated transcription by RNA polymerase II. Although it is well known that the TAF N-terminal domain (TAND) at the amino-terminus of the TAF1 protein binds to TBP and thereby inhibits TBP function in vitro, the physiological role of this domain remains obscure. In our previous study, we screened for mutations that cause lethality when co-expressed with the TAF1 gene lacking TAND (taf1-DeltaTAND) and identified two DeltaTAND synthetic lethal (nsl) mutations as those in the SPT15 gene encoding TBP.

Impairment of the DNA binding activity of the TATA-binding protein renders the transcriptional function of Rvb2p/Tih2p, the yeast RuvB-like protein, essential for cell growth.

In Saccharomyces cerevisiae, two highly conserved proteins, Rvb1p/Tih1p and Rvb2p/Tih2p, have been demonstrated to be major components of the chromatin-remodeling INO80 complex. The mammalian orthologues of these two proteins have been shown to physically associate with the TATA-binding protein (TBP) in vitro but not clearly in vivo. Here we show that yeast proteins interact with TBP under both conditions.

Apatite-forming ability and mechanical properties of CaO-free poly(tetramethylene oxide) (PTMO)-TiO2 hybrids treated with hot water.

Poly(tetramethylene oxide) (PTMO)-TiO(2) hybrids were prepared by a sol-gel method from triethoxysilane-functionalized PTMO (Si-PTMO) and tetraisopropyltitanate with weight ratios of 30/70, 40/60 and 50/50 (hybrids PT30, PT40 and PT50, respectively), and subsequently subjected to a hot-water treatment at 95 degrees C for 2 d. All the obtained hybrids were amorphous before the hot-water treatment, and precipitated nanosized anatase after the hot-water treatment. The amount of precipitated anatase increased with decreasing PTMO content.

A comparative study between in vivo bone ingrowth and in vitro apatite formation on Na2O-CaO-SiO2 glasses.

This study compared in vivo bioactivity with the in vitro apatite-forming ability of biomaterials. Granules of five kinds of P(2)O(5)-free Na(2)O-CaO-SiO(2) glasses, showing different apatite-forming ability in simulated body fluid (SBF), were implanted into a defect on the femoral condyle of rabbits. Bone ingrowth was evaluated using scanning electron microscopy among five kinds of glasses at 1, 2, 3, 6, and 12 weeks.

Formation and growth of clusters in conventional and new kinds of simulated body fluids.

Simulated body fluid (SBF) with ion concentrations approximately equal to those of human blood plasma has been widely used for the in vitro assessment of the bioactivity of artificial materials and for the formation of bonelike apatite on various substrates. Ion concentrations of conventional SBF (c-SBF) are, however, not exactly equal to those of blood plasma, and hence the apatite formed in c-SBF is not the same as bone apatite in its composition and structure. Recently, the present authors prepared new kinds of SBFs (r-SBF, i-SBF, and m-SBF) with ion concentrations nearer to those of blood plasma.