Stochastic electrotransport selectively enhances the transport of highly electromobile molecules.

Nondestructive chemical processing of porous samples such as fixed biological tissues typically relies on molecular diffusion. Diffusion into a porous structure is a slow process that significantly delays completion of chemical processing. Here, we present a novel electrokinetic method termed stochastic electrotransport for rapid nondestructive processing of porous samples.

Study of the air-water interfacial properties of biodegradable polyesters and their block copolymers with poly(ethylene glycol).

It has been reported that the surface pressure-area isotherm of poly(D,L-lactic acid-ran-glycolic acid) (PLGA) at the air-water interface exhibits several interesting features: (1) a plateau at intermediate compression levels, (2) a sharp rise in surface pressure upon further compression, and (3) marked surface pressure-area hysteresis during compression-expansion cycles. To investigate the molecular origin of this behavior, we conducted an extensive set of surface pressure and AFM imaging measurements with PLGA materials having several different molecular weights and also a poly(D,L-lactic acid-ran-glycolic acid-ran-caprolactone) (PLGACL) material in which the caprolactone monomers were incorporated as a plasticizing component. The results suggest that (i) the plateau in the surface pressure-area isotherm of PLGA (or PLGACL) occurs because of the formation (and collapse) of a continuous monolayer of the polymer under continuous compression; (ii) the PLGA monolayer becomes significantly resistant to compression at high compression because under that condition the collapsed domains become large enough to become glassy (such behavior was not observed in the nonglassy PLGACL sample); and (iii) the isotherm hysteresis is due to a coarsening of the collapsed domains that occurs under high-compression conditions.

Water is a poor solvent for densely grafted poly(ethylene oxide) chains: a conclusion drawn from a self-consistent field theory-based analysis of neutron reflectivity and surface pressure-area isotherm data.

By use of a combined experimental and theoretical approach, a model poly(ethylene oxide) (PEO) brush system, prepared by spreading a poly(ethylene oxide)-poly(n-butyl acrylate) (PEO-PnBA) amphiphilic diblock copolymer onto an air-water interface, was investigated. The polymer segment density profiles of the PEO brush in the direction normal to the air-water interface under various grafting density conditions were determined by using the neutron reflectivity (NR) measurement technique. To achieve a theoretically sound analysis of the reflectivity data, we used a data analysis method that utilizes the self-consistent field (SCF) theoretical modeling as a tool for predicting expected reflectivity results for comparison with the experimental data.

Development of highly porous large PLGA microparticles for pulmonary drug delivery.

We report a new process of making highly-porous large polymeric microparticles for local drug delivery to the lungs by inhalation. Poly(lactic-co-glycolic acid) (PLGA) microparticles (average diameter, 10-20 microm) were made by the double-emulsion method. To impart favorable aerodynamic properties, an effervescent salt ammonium bicarbonate (ABC) was included in the internal aqueous phase.