Reconsideration of Enamel Etching Protocols for Universal Adhesives: Effect of Etching Method and Etching Time.

Purpose: To evaluate whether different etching methods with reduced etching times would improve the enamel bonding efficacy of universal adhesives.

Materials And Methods: Three enamel etching methods were evaluated - 1. phosphoric acid ester monomer etching (PPM); 2.

Influence of surface wetness on bonding effectiveness of universal adhesives in etch-and-rinse mode.

The purpose of this study was to evaluate whether surface wetness would influence the bonding effectiveness of universal adhesives in etch-and-rinse mode. All-Bond Universal (AB), G-Premio Bond (GP), Prime & Bond Active (PB), and Scotchbond Universal Adhesive (SU) were evaluated. Initial bond strengths and bond-fatigue strengths of universal adhesives to both wet and dry enamel and dentin in etch-and-rinse mode were determined.

Wear of resin composites: Current insights into underlying mechanisms, evaluation methods and influential factors.

The application of resin composites in dentistry has become increasingly widespread due to the increased aesthetic demands of patients, improvements in the formulation of resin composites, and the ability of these materials to bond to tooth structures, together with concerns about dental amalgam fillings. As resistance to wear is an important factor in determining the clinical success of resin composite restoratives, this review article defines what constitutes wear and describes the major underlying phenomena involved in this process. Insights are further included on both and tests used to determine the wear resistance of resin composite and the relationships between these tests.

Comparison of enamel bond fatigue durability of universal adhesives and two-step self-etch adhesives in self-etch mode.

Purpose: To comparatively evaluate universal adhesives and two-step self-etch adhesives for enamel bond fatigue durability in self-etch mode.

Methods: Three universal adhesives (Clearfil Universal Bond; G-Premio Bond; Scotchbond Universal Adhesive) and three two-step self-etch adhesives (Clearfil SE Bond; Clearfil SE Bond 2; OptiBond XTR) were used. The initial shear bond strength and shear fatigue strength of the adhesive to enamel in self-etch mode were determined.

Comparison of enamel bond fatigue durability between universal adhesives and two-step self-etch adhesives: Effect of phosphoric acid pre-etching.

The effect of phosphoric acid pre-etching on enamel bond fatigue durability of universal adhesives and two-step self-etch adhesives was investigated. Four universal adhesives and three two-step self-etch adhesives were used. The initial shear bond strengths and shear fatigue strengths to enamel with and without phosphoric acid pre-etching using the adhesives were determined.

Influence of application method on surface free-energy and bond strength of universal adhesive systems to enamel.

The aim of the present study was to determine the influence of different adhesive application methods and etching modes on enamel bond effectiveness of universal adhesives using shear bond strength (SBS) testing and surface free-energy (SFE) measurements. The adhesives Scotchbond Universal, All-Bond Universal, Adhese Universal, and G-Premio Bond were used. Prepared bovine enamel specimens were divided into four groups, based on type of adhesive, and subjected to the following surface treatments: (i) total-etch mode with active application; (ii) total-etch mode with inactive application; (iii) self-etch mode with active application; and (iv) self-etch mode with inactive application.

Influence of photoirradiation conditions on dentin bond durability and interfacial characteristics of universal adhesives.

The influence of photoirradiation conditions on dentin bond durability and interfacial characteristics of universal adhesives was investigated. Universal adhesives were applied to the dentin surfaces and photoirradiated with 100 mW/cm for 40 s, 200 mW/cm for 20 s, and 400 mW/cm for 10 s. A resin composite was bonded to dentin to determine shear bond strength after 24 h water storage and 30,000 thermal cycles, and water contact angle of cured adhesive were measured by the sessile drop method.

Influence of surface treatment of contaminated lithium disilicate and leucite glass ceramics on surface free energy and bond strength of universal adhesives.

This study investigates the influence of surface treatment of contaminated lithium disilicate and leucite glass ceramic restorations on the bonding efficacy of universal adhesives. Lithium disilicate and leucite glass ceramics were contaminated with saliva, and then cleaned using distilled water (SC), or 37% phosphoric acid (TE), or hydrofluoric acid (CE). Specimens without contamination served as controls.

Influence of light intensity on surface-free energy and dentin bond strength of single-step self-etch adhesives.

In this study, we investigated the influence of light intensity on the surface-free energy and dentin bond strength of single-step selfetch adhesives. The adhesives were applied to the dentin surfaces of bovine mandibular incisors and cured with light intensities of 0 (no irradiation), 200, 400, and 600 mW/cm(2). Surface-free energies were determined by measuring the contact angles of three test liquids placed on the cured adhesives.

Evaluation of a calcium phosphate desensitizer using an ultrasonic device.

This study evaluated the effect of a calcium phosphate desensitizer on the demineralization of bovine dentin by measuring changes in transmitted ultrasonic velocity. Bovine dentin specimens with and without application of desensitizer were immersed in 0.1 M lactic-acid buffer solution (pH 4.