Hybrid Alginate-Brushite Beads Easily Catalyze the Knoevenagel Condensation On-Water.

An innovative hybrid organic-inorganic material composed of alginate-brushite xerogel beads was successfully applied for the catalysis of the Knoevenagel condensation. The catalyst was derived from phosphated alginate xerogel microspheres formed from the ionotropic gelling effect of phosphated alginate. To this end, alginate was phosphated by the addition of diammonium hydrogen phosphate in a 1% w/w alginate gel.

Sulfated Well-Defined Mesoporous Nanostructured Zirconia for Levulinic Acid Esterification.

Well-organized zirconia (ZrO) nanoparticles forming mesoporous materials have been successfully synthesized via a facile micelle-templating method using cetyltrimethylammonium bromide as a structure-directing template to control the nucleation/growth process and porosity. The systematic use of such a surfactant in combination with a microwave-assisted solvothermal (cyclohexane/water) reaction enabled the control of pore size in a narrow-size distribution range (3-17 nm). The effect of solvent mixture ratio on the porosity of the synthesized oxide was determined, and the controlled growth of zirconia nanoparticles was confirmed by means of powder X-ray diffraction, small-angle X-ray scattering, transmission electron microscopy, selected area electron diffraction, high-resolution transmission electron microscopy, X-ray photoelectron spectroscopy, thermogravimetric analysis, and Fourier transform infrared spectroscopy as well as N physisorption isotherm analysis.

Effective Catalytic Delignification and Fractionation of Lignocellulosic Biomass in Water over ZnVO Mixed Oxide.

The conversion of poplar wood biomass to highly value-added chemicals and molecular building blocks was achieved by using the dispersed mixed oxide ZnVO (ZVO) in water under 100 kPa of 10% O/N at 160, 180, and 200 °C for 4 h. This nanostructured mixed oxide was prepared via the precipitation process and then characterized by several techniques. The results showed that this mixed oxide has interesting catalytic properties and is a versatile catalyst for biomass delignification and lignin and hemicellulose depolymerization.