Lasing action and optical amplification in Nd3+ doped electrooptic lanthanum lead zirconate titanate ceramics.

Both single-pass gain and lasing action at 1064.4 nm were observed in ceramic gain media of neodymium doped lanthanum-modified lead zirconate titanate, which exhibits good electrooptic (EO) effect from visible through mid-wave IR band (400 nm to 5.5 µm).

Wavelength translation based on photoinduced broadband absorption in Nd3+ -doped lanthanum lead zirconate titanate ceramics.

A correlation between a photoinduced broadband absorption (BBA) and a strong long persistent optoenergy storage (LPOES), both evident in ceramic plates of neodymium-doped lanthanum-modified lead zirconate titanate (Nd:PLZT), has been proposed and verified experimentally. As a direct evidence of the suggested correlation, a 3.0 dB gain was obtained with a preilluminated Nd:PLZT plate by simply heating up the plate to 60 degrees C.