Photodeposition-Based Synthesis of TiO@IrO Core-Shell Catalyst for Proton Exchange Membrane Water Electrolysis with Low Iridium Loading.

The widespread application of green hydrogen production technologies requires cost reduction of crucial elements. To achieve this, a viable pathway to reduce the iridium loading in proton exchange membrane water electrolysis (PEMWE) is explored. Herein, a scalable synthesis method based on a photodeposition process for a TiO@IrO core-shell catalyst with a reduced iridium content as low as 40 wt.

Internal Crack Initiation and Growth Starting from Artificially Generated Defects in Additively Manufactured Ti6Al4V Specimen in the VHCF Regime.

The aim of the present work was to investigate the 'fine granular area' (FGA) formation based on artificially generated internal defects in additively manufactured Ti6Al4V specimens in the early stage of fatigue crack growth in the 'very high cycle fatigue' (VHCF) regime. Fatigue tests were performed with constant amplitude at pure tension-compression loading ( = -1) using an ultrasonic fatigue testing setup. Failed specimens were investigated using optical microscopy, high-resolution 'scanning electron microscopy' (SEM), and 'focused ion beam' (FIB) techniques.