Apatite-forming ability and mechanical properties of PTMO-modified CaO-SiO2-TiO2 hybrids derived from sol-gel processing.

Hydrolysis and polycondensation of triethoxysilane end-capped Poly (tetramethylene oxide) (Si-PTMO), tetraethoxysilane (TEOS), tetraisopropyltitanate (TiPT) and calcium nitrate (Ca(NO(3))(2)) gave transparent monolithics of PTMO-modified CaO-SiO(2)-TiO(2) hybrids. The samples with (TiPT)/(TEOS+TiPT) molar ratios from 0 to 0.20 under constant ratio of (Si-PTMO)/(TEOS+TiPT) of 2/3 in weight were prepared.

Apatite-forming ability and mechanical properties of PTMO-modified CaO-SiO2 hybrids prepared by sol-gel processing: effect of CaO and PTMO contents.

Transparent monolithics of triethoxysilane end-capped poly(tetramethylene oxide) (Si-PTMO)-modified CaO-SiO2 hybrids were successfully synthesized by hydrolysis and polycondensation of Si-PTMO, tetraethoxysilane (TEOS) and calcium nitrate. As for the samples with varying (Ca(NO3)2)/(TEOS) molar ratios under constant ratio of (Si-PTMO)/(TEOS) of 2/3 in weight. the apatite-forming ability in a simulated body fluid (SBF) which is indicative of bioactivity.