Effects of chromium and nitrogen content on the microstructures and mechanical properties of as-cast Co-Cr-Mo alloys for dental applications.

The microstructure and mechanical properties of as-cast Co-(20-33)Cr-5Mo-N alloys were investigated to develop ductile Co-Cr-Mo alloys without Ni addition for dental applications that satisfy the requirements of the type 5 criteria in ISO 22674. The effects of the Cr and N contents on the microstructure and mechanical properties are discussed. The microstructures were evaluated using scanning electron microscopy with energy-dispersive X-ray spectroscopy (EDS), X-ray diffractometry (XRD), and electron back-scattered diffraction pattern analysis.

Evaluation of the static frictional coefficients of Co-Cr and gold alloys for cone crown telescope denture retainer applications.

The static frictional coefficients (SFC) of a Co-Cr and a gold alloys were evaluated for the application of a cone crown telescope system in removable prosthesis. The SFCs of the Co-Cr alloy were lower than those of the gold alloy. The SFC of the gold alloy decreased by annealing at 85°C in air and was restored by re-polishing, although that of the Co-Cr alloy was stable irrespective of the annealing.