Evaluation of depth of dislocation visibility in SEM electron channeling contrast imaging in Ti-6Al-4V alloy using serial sectioning method.

In this study, we conducted a quantitative evaluation of dislocation density by scanning electron microscopy electron channeling contrast imaging for α grains of a Ti-6Al-4V alloy deformed at room temperature. The depth of visibility of dislocations is experimentally measured as 140 to 160 nm by a serial sectioning observation. This result is compared with the theoretical value and applied to evaluate dislocation density.