[Raman characterization of rutile phase transitions under high-pressure and high-temperature].

The pressure-induced phase transition of rutile-structured TiO2 was investigated by in-situ Raman spectrum method in a laser-heated diamond anvil cell (DAC). The experiment was conducted at 35 GPa under quasihydrostatic conditions using argon as medium. At room temperature, the rutile-type TiO2 begins to transform to baddeleyite-type phase at 13.

[Infrared spectroscopic study of Changbaishan diatomite].

Changbaishan diatomite was treated under the conditions of temperature from 100 to 1330 degrees C, and examined by infrared spectroscopy applying the KBr-technique. In the range from 250 to 1500 cm(-1), the spectra of the samples at 100 to 1100 degrees C show the same three characteristic broad bands at 1100, 801 and 471 cm(-1), which are similar to amorphous silica. Besides the above three broad bands, the spectra of 1200 and 1330 degrees C treated samples exhibit three new bands at 618, 386 and 301 cm(-1), which indicate that the diatornite transforms into cristobalite.