Experiments to understand crystallization of levitated high temperature silicate melt droplets under low vacuum conditions.

We report experiments on crystallization of highly undercooled forsterite melt droplets under atmospheric and sub-atmospheric pressure conditions. Experiments have been conducted under non-contact conditions using the principles of aero-dynamic levitation. Real time dynamics of solidification, along with the transient evolution of surface textures, have been recorded using high speed camera for three cooling rates.

Adherent and Conformal Zn(S,O,OH) Thin Films by Rapid Chemical Bath Deposition with Hexamethylenetetramine Additive.

ZnS is a wide band gap semiconductor whose many applications, such as photovoltaic buffer layers, require uniform and continuous films down to several nanometers thick. Chemical bath deposition (CBD) is a simple, low-cost, and scalable technique to deposit such inorganic films. However, previous attempts at CBD of ZnS have often resulted in nodular noncontinuous films, slow growth rates at low pH, and high ratio of oxygen impurities at high pH.

High-efficiency solution-processed Cu2ZnSn(S,Se)4 thin-film solar cells prepared from binary and ternary nanoparticles.

A new solution-based method to fabricate Cu(2)ZnSn(S,Se)(4) (CZTSSe) thin films is presented. Binary and ternary chalcogenide nanoparticles were synthesized and used as precursors to form CZTSSe thin films. The composition of the CZTSSe films can be easily controlled by adjusting the ratio of the nanoparticles used.

Synthetic principles directing charge transport in low-band-gap dithienosilole-benzothiadiazole copolymers.

Given the fundamental differences in carrier generation and device operation in organic thin-film transistors (OTFTs) and organic photovoltaic (OPV) devices, the material design principles to apply may be expected to differ. In this respect, designing organic semiconductors that perform effectively in multiple device configurations remains a challenge. Following "donor-acceptor" principles, we designed and synthesized an analogous series of solution-processable π-conjugated polymers that combine the electron-rich dithienosilole (DTS) moiety, unsubstituted thiophene spacers, and the electron-deficient core 2,1,3-benzothiadiazole (BTD).

Aesthetically pleasing conjugated polymer:fullerene blends for blue-green solar cells via roll-to-roll processing.

The practical application of organic photovoltaic (OPV) cells requires high throughput printing techniques in order to attain cells with an area large enough to provide useful amounts of power. However, in the laboratory screening of new materials for OPVs, spin-coating is used almost exclusively as a thin-film deposition technique due its convenience. We report on the significant differences between the spin-coating of laboratory solar cells and slot-die coating of a blue-green colored, low bandgap polymer (PGREEN).

PbSe nanocrystal-based infrared-to-visible up-conversion device.

Low-cost hybrid up-conversion devices with infrared sensitivity to 1.5 μm were obtained by integrating a colloidal PbSe nanocrystal near-infrared sensitizing layer on a green phosphorescent organic light emitting diode. A ZnO nanocrystal hole blocking layer is incorporated in the devices for keeping the device off in the absence of IR excitation.

Efficient green solar cells via a chemically polymerizable donor-acceptor heterocyclic pentamer.

In this contribution, we report on bulk-heterojunction solar cells using a solution-processable neutral green conjugated copolymer based on 3,4-dioxythiophene and 2,1,3-benzothiadiazole as the donor and [6,6]phenyl-C61 butyric acid methyl ester (PCBM) as the acceptor. We have found that the short-circuit current is very sensitive to the composition of the donor-acceptor blend and it increases with increasing acceptor concentration. The device with a donor-acceptor ratio of 1:8 gives the best performance with a short-circuit current of 5.

Shape control of PbSe nanocrystals using noble metal seed particles.

We demonstrate that the shape of PbSe nanocrystals can be controlled systematically by seeding their growth with noble metal nanoparticles (Au, Ag, or Pd) and varying the seed and precursor concentrations. Cylinders (quantum rods), cubes, crosses, stars, and branched structures were produced in high yield at 150 degrees C in reaction times of a few minutes. Although their absorption spectrum does not exhibit sharp features, the quantum rods exhibit significant photogeneration efficiency, enabling infrared sensitization of a polymeric photoconductive nanocomposite.