Surface structure of chitosan and hybrid chitosan-amylose films-restoration of the antibacterial properties of chitosan in the amylose film.

The surface structure of films prepared by casting aqueous solutions of mixtures of water soluble chitosan (WSC) and amylose as well as a fully deacetylated chitosan was studied. Zeta potential measurements indicated that the surface of WSC and fully deacetylated chitosan films is positively charged but very weakly, whereas, a film of amylose blended with WSC exhibited an obvious positive charge. X-ray photoelectron spectra of these films suggest that less amino groups are exposed on the surface of WSC and fully deacetylated chitosan films, whereas, more amino groups are exposed on the surface of a WSC film blended with amylose.

Effect of addition of water-soluble chitin on amylose film.

Amylose films blended with chitosan, which were free from additives such as acid, salt, and plasticizer, were prepared by casting mixtures of an aqueous solution of an enzymatically synthesized amylose and that of water-soluble chitin (44.1% deacetylated). The presence of a small amount of chitin (less than 10%) increased significantly the permeability of gases (N2, O2, CO2, C2H4) and improved the mechanical parameters of amylose film; particularly, the elastic modulus and elongation of the blend films were larger than those of amylose or chitin films.