Interspecific variation in patterns of adhesion of marine fouling to silicone surfaces.

The adhesion of six fouling organisms: the barnacle Balanus eburneus, the gastropod mollusc Crepidulafornicata, the bivalve molluscs Crassostrea virginica and Ostrea/Dendrostrea spp., and the serpulid tubeworms Hydroides dianthus and H. elegans, to 12 silicone fouling-release surfaces was examined.

Contact angle anomalies indicate that surface-active eluates from silicone coatings inhibit the adhesive mechanisms of fouling organisms.

Silicone coatings with critical surface tensions (CST) between 20 and 30 mN m-1 more easily release diverse types of biofouling than do materials of higher and lower CST. Oils added to these coatings selectively further diminish the attachment strengths of different marine fouling organisms, without significantly modifying the initial CST. In a search for the mechanisms of this improved biofouling resistance, the interfacial instabilities of four silicone coatings were characterised by comprehensive contact angle analyses, using up to 12 different diagnostic fluids selected to mimic the side chain chemistries of the common amino acids of bioadhesive proteins.

The effects of silicone fluid additives and silicone elastomer matrices on barnacle adhesion strength.

Barnacle adhesion strength was used to screen seventy-seven polydimethylsiloxane elastomeric coatings for fouling-release properties. The test coatings were designed to investigate the effect on barnacle adhesion strength of silicone fluid additive type, additive location, additive molecular weight, additive loading level, mixtures of additives, coating matrix type and coating fillers. The type of silicone fluid additive was the primary controlling factor in barnacle fouling-release.

Silicone foul release coatings: effect of the interaction of oil and coating functionalities on the magnitude of macrofouling attachment strengths.

Silicone biofouling release coatings have been shown to be an effective method of combating fouling. Nearly all silicone foul release coatings are augmented with an oil additive to decrease macrofouling attachment strength. This paper addresses the effect of the type of oil that is incorporated into the silicone coating and the type of silicone coating itself (silica vs calcium carbonate filled) on macrofouling adhesion strengths to the coating.

Structure-property relationships of silicone biofouling-release coatings: effect of silicone network architecture on pseudobarnacle attachment strengths.

Model silicone foul-release coatings with controlled molecular architecture were evaluated to determine the effect of compositional variables such as filler loading and crosslink density on pseudobarnacle attachment strength. Pseudobarnacle adhesion values correlated with filler loadings in both condensation and hydrosilylation-cured silicones. Variation of crosslink density of hydrosilylation-cured silicones had an insignificant effect on attachment strength.