The impact of the heating rate on the Ni content at the surface of the oxide layer of biomedical NiTi is explored. Heat treatment emulating common shape-setting procedures was performed by means of conventional and inductive heating for similar annealing time and temperature, applying various heating rates from ~0.25 K s(-1) to 250 K s(-1).
View Article and Find Full Text PDFThe effect of annealing and deformation on short-term (21days) and long-term (8months) Ni release from biomedical NiTi wires is studied. The deformation of annealed NiTi wires causes cracking and flaking of the surface oxide layer. Flaking of oxide particles does not uncover the Ni-rich layer underneath the surface oxide layer, since at sites where flaking occurs, a thin (∼25nm) layer of oxide remains on top of this Ni-rich layer.